采用一浴水媒法制备了羧甲基改性粘胶非织造布(CM-VN),通过 X 射线衍射、扫描电子显微镜研究了羧甲基改性后粘胶非织造布中纤维结构的变化,并考察了取代度对 CM-VN 吸水性、透气性、扩散性和力学性能的影响。实验结果表明,随着 CM-VN取代度的升高,其结晶度逐渐降低,吸水性能显著增强,透气性逐渐降低,扩散性能先升高后降低,断裂强力和断裂伸长率均呈现先降低后升高的趋势；当取代度为0.35时,CM-VN吸水后形成均匀半透明的水凝胶体,其吸水性达到25.44g/g(蒸馏水)和24.38g/g (生理盐水),断裂强力和断裂伸长率分别为85.7N 和47.5%,并且具有良好的透气性和阻塞性,能够作为一种优良的吸附材料用于制备高性能医用敷料。
채용일욕수매법제비료최갑기개성점효비직조포(CM-VN),통과 X 사선연사、소묘전자현미경연구료최갑기개성후점효비직조포중섬유결구적변화,병고찰료취대도대 CM-VN 흡수성、투기성、확산성화역학성능적영향。실험결과표명,수착 CM-VN취대도적승고,기결정도축점강저,흡수성능현저증강,투기성축점강저,확산성능선승고후강저,단렬강력화단렬신장솔균정현선강저후승고적추세；당취대도위0.35시,CM-VN흡수후형성균균반투명적수응효체,기흡수성체도25.44g/g(증류수)화24.38g/g (생리염수),단렬강력화단렬신장솔분별위85.7N 화47.5%,병차구유량호적투기성화조새성,능구작위일충우량적흡부재료용우제비고성능의용부료。
Carboxymethyl viscose nonwoven (CM-VN)was successfully prepared in aqueous medium through one bath process.The structure of fiber in CM-VN was studied by X-ray diffraction (XRD)and scanning electron microscope (SEM),and the influence of substitution degree (DS)on water absorbency,water vapor permeability, water diffusion property and mechanical property of CM-VN was investigated.As the DS of CM-VN increased,its crystallinity degree decreased gradually,water absorbency enhanced remarkably,water vapor permeability and water diffusion property decreased smoothly,and the breaking strength first increased then decreased. With DS of 0.35,CM-VN could form uniform and semitransparent hydrogel after absorbing water. And its water absorbency reached 25.44g/g (distilled water)and 24.38g/g (normal saline).The breaking strength and breaking elongation of the CM-VN were respectively 85.7 N and 47.5%.In addition,the CM-VN has good water vapor permeability and blocking performance.Therefore,CM-VN could be used as absorbing material for the preparation of high performance medical dressing.