以涤纶纱线为基材制备涤纶/聚苯胺导电纱线。采用正交试验分析 pH 值、苯胺、过硫酸铵的用量对导电性能的影响。通过对比实验观察碱减量预处理的效果；利用万用表对复合纱线导电性能进行测量。结果表明：碱减量预处理非常必要，当 pH 值为2~3，苯胺用量为10 g，过硫酸铵质量为2g 时导电纱线的电阻率最低，为96Ω·cm。
이조륜사선위기재제비조륜/취분알도전사선。채용정교시험분석 pH 치、분알、과류산안적용량대도전성능적영향。통과대비실험관찰감감량예처리적효과；이용만용표대복합사선도전성능진행측량。결과표명：감감량예처리비상필요，당 pH 치위2~3，분알용량위10 g，과류산안질량위2g 시도전사선적전조솔최저，위96Ω·cm。
Polyaniline/ Dacron conductive composite yarn was prepared with polyester yarn as base material. By using of orthogonal experiment,the effect of pH,aniline and ammonium persulfate on conductive performance of composite yarn is studied. By contrast experiment to observe the effect of alkali deweighting pretreatment;Using the multimeter to measure composite yarn conductive properties. The results show that alkali deweighting pretreatment is necessary;When the conditions are as follows:pH is between 2 ~ 3,The amount of aniline is 10 g,and ammonium persulfate is 3 g,The resistivity of composite yarn is as low as 96 Ω·cm.