制备了一种注射型壳聚糖(CS)温敏相变复合材料，首先采用乳化-化学交联法，以戊二醛为交联剂，制备包载甲氨蝶呤(MTX)的壳聚糖微球，然后采用离子交联法，向 CS 溶液中滴加50％甘油磷酸钠溶液，制备CS温敏水凝胶.将CS载药微球分散于水凝胶中，制得温敏相变复合材料.结果表明，所制得的微球载药量为12．98％，包封率为32．66％，且粒径均一，分散性良好，具有良好的通针性；水凝胶在37℃下1 min内可发生相变，由溶胶转变为凝胶，具有良好的温度敏感性；制备的温敏相变复合材料具有良好的原位注射性，且4 h 内药物释放率为35．65％，缓释效果明显.
제비료일충주사형각취당(CS)온민상변복합재료，수선채용유화-화학교련법，이무이철위교련제，제비포재갑안접령(MTX)적각취당미구，연후채용리자교련법，향 CS 용액중적가50％감유린산납용액，제비CS온민수응효.장CS재약미구분산우수응효중，제득온민상변복합재료.결과표명，소제득적미구재약량위12．98％，포봉솔위32．66％，차립경균일，분산성량호，구유량호적통침성；수응효재37℃하1 min내가발생상변，유용효전변위응효，구유량호적온도민감성；제비적온민상변복합재료구유량호적원위주사성，차4 h 내약물석방솔위35．65％，완석효과명현.
In this article,the inj ectable thermo-sensitive chitosan-based complexity was prepared.First,Metho-trexate (MTX)-loaded chitosan microspheres were prepared with emulsion-chemical cross-linking method using glutaraldehyde as crosslinking agents.CS thermo-sensitive hydrogel was prepared by CS and gycerophosphate using ionic crosslinking method.The thermo-sensitive chitosan-based complexity was composed by CS micro-spheres and CS hydrogel.The results indicated that the drug-loading efficiency and encapsulation efficiency of CS microspheres were 12.98% and 32.66%,respectively.The microspheres prepared in this study had uniform particle size,good dispersibility and could be inj ected through needles.The phase could change from the sol state to a gel state at 3 7 ℃ in 1 min,which indicated the hydrogel prepared in this article had good thermo-sen-sitivity.The thermo-sensitive chitosan-based complexity had a good ability of inj ection.In vitro releasing prop-erties of MTX were investigated and the results indicated that 3 5 .6 5% of the total MTX in the thermo-sensitive chitosan-based complexity was released in the first 4 h.The complexity had an ideal releasing effect.