植物源防腐剂因其环保、广谱、高效等特点越来越受到木材防腐行业的重视,从微观层面探索香樟提取物影响木材腐朽的机理是发展利用植物源防腐剂的重要基础。试验采用香樟木质部的四种溶剂提取物、ACQ及樟脑配制成防腐剂进行防腐试验,结果表明:10%浓度的香樟木质部甲醇提取物以及4%浓度的ACQ处理试件均达到I级强耐腐水平,4%樟脑、10%香樟乙酸乙酯和10%丙酮提取物处理的试件达到Ⅱ级耐腐水平。通过XRD对比发现结晶区2θ衍射强度由大到小的顺序为:10%蒸馏水提取物处理材、马尾松素样、10%丙酮提取物处理材、10%甲醇提取物处理材、10%乙酸乙酯提取物处理材,四种香樟木质部提取物的防腐效果与相对结晶度大小呈正相关。通过FT IR研究发现表征纤维素和半纤维素的特征峰值越低,则被降解的量也越大,相对应的防腐剂防腐效果越差。处理试件中表征木质素的一系列特征峰峰高与未处理材相比有所升高。香樟甲醇提取物以及ACQ处理试件的 I1510/I1738, I1510/I1374, I1510/I1160的比值最小,证明褐腐菌对其综纤维素的降解能力最弱,防腐效果最好。
植物源防腐劑因其環保、廣譜、高效等特點越來越受到木材防腐行業的重視,從微觀層麵探索香樟提取物影響木材腐朽的機理是髮展利用植物源防腐劑的重要基礎。試驗採用香樟木質部的四種溶劑提取物、ACQ及樟腦配製成防腐劑進行防腐試驗,結果錶明:10%濃度的香樟木質部甲醇提取物以及4%濃度的ACQ處理試件均達到I級彊耐腐水平,4%樟腦、10%香樟乙痠乙酯和10%丙酮提取物處理的試件達到Ⅱ級耐腐水平。通過XRD對比髮現結晶區2θ衍射彊度由大到小的順序為:10%蒸餾水提取物處理材、馬尾鬆素樣、10%丙酮提取物處理材、10%甲醇提取物處理材、10%乙痠乙酯提取物處理材,四種香樟木質部提取物的防腐效果與相對結晶度大小呈正相關。通過FT IR研究髮現錶徵纖維素和半纖維素的特徵峰值越低,則被降解的量也越大,相對應的防腐劑防腐效果越差。處理試件中錶徵木質素的一繫列特徵峰峰高與未處理材相比有所升高。香樟甲醇提取物以及ACQ處理試件的 I1510/I1738, I1510/I1374, I1510/I1160的比值最小,證明褐腐菌對其綜纖維素的降解能力最弱,防腐效果最好。
식물원방부제인기배보、엄보、고효등특점월래월수도목재방부행업적중시,종미관층면탐색향장제취물영향목재부후적궤리시발전이용식물원방부제적중요기출。시험채용향장목질부적사충용제제취물、ACQ급장뇌배제성방부제진행방부시험,결과표명:10%농도적향장목질부갑순제취물이급4%농도적ACQ처리시건균체도I급강내부수평,4%장뇌、10%향장을산을지화10%병동제취물처리적시건체도Ⅱ급내부수평。통과XRD대비발현결정구2θ연사강도유대도소적순서위:10%증류수제취물처리재、마미송소양、10%병동제취물처리재、10%갑순제취물처리재、10%을산을지제취물처리재,사충향장목질부제취물적방부효과여상대결정도대소정정상관。통과FT IR연구발현표정섬유소화반섬유소적특정봉치월저,칙피강해적량야월대,상대응적방부제방부효과월차。처리시건중표정목질소적일계렬특정봉봉고여미처리재상비유소승고。향장갑순제취물이급ACQ처리시건적 I1510/I1738, I1510/I1374, I1510/I1160적비치최소,증명갈부균대기종섬유소적강해능력최약,방부효과최호。
Four kinds of extracts from the xylem of C .Camphora ,ACQ and camphor were selected to make wood preservatives for laboratory toxicity test of wood preservatives for decay fungus .The results showed that the treated blocks with 4% ACQ and 10% methanol extracts could meet the demand of degree Ⅰ of preservation and showed strong resistance to brown-rot fungus at-tack .The wood treated with 4% camphor extracts ,10% ethyl acetate extracts ,and 10% acetone extracts reached the demand of degree Ⅱ and showed moderate decay resistance .The blocks treated with 10% hot water extracts and untreated samples meet the demand of degree Ⅲ .Through XRD comparison ,the author was found that the preservative effects of four extracts are pro-portional to the degree of crystallinity .Crystallization fields 2θdiffraction angle were ordered from larger to little as 10% hot wa-ter extracts>untreated samples>10% acetone extracts>10% methanol extracts>10% ethyl acetate extracts .According to FT-IR analysis ,the amount of degraded cellulose and hemicellulose increased with the decline of characteristic absorption peak at 1 374 ,1 160 ,1 106 ,1 056 and 897 cm -1 ,meaning that the preservative effect of corresponding preservatives were getting worse .The peak height of characterization of lignin is higher compared to the untreated wood .I1510/I1738 ,I1510/I1374 ,I1510/I1 160 of the treated blocks with 10% methanol extracts and 4% ACQ are the smallest in all the treated blocks ,which proved that the degradation ability of brown -rot fungus to the holocellulose is the weakest ,and the wood preservative is best .