磁化%W6Mo5Cr4V2高速钢刀具%加工质量%积屑瘤
磁化%W6Mo5Cr4V2高速鋼刀具%加工質量%積屑瘤
자화%W6Mo5Cr4V2고속강도구%가공질량%적설류
magnetization%W6Mo5Cr4V2 high-speed steel tool%processing quality%built-up edge
利用自制的交流磁化装置对W6Mo5Cr4V2高速钢刀具进行了磁化处理,并在通用机床上使用经磁化处理的高速钢刀具及未经磁化处理的高速钢刀具进行了切削实验,实验结果表明:与普通高速钢刀具相比,经磁化处理后的W6Mo5Cr4V2高速钢刀具,其切削工件表面粗糙度得到改善。同时,磁化时间及磁化频率应视为磁化处理中的关键调节参数,不同磁化时间及频率下的W6Mo5Cr4V2高速钢刀具的切削性能有所不同,在低频下的效果更好。另外,实验结果也表明:经交流磁化处理的W6Mo5Cr4V2高速钢刀具能够降低切削过程中的切削力并抑制积屑瘤的产生,从而增加刀具的使用寿命并提高刀具的加工质量。
利用自製的交流磁化裝置對W6Mo5Cr4V2高速鋼刀具進行瞭磁化處理,併在通用機床上使用經磁化處理的高速鋼刀具及未經磁化處理的高速鋼刀具進行瞭切削實驗,實驗結果錶明:與普通高速鋼刀具相比,經磁化處理後的W6Mo5Cr4V2高速鋼刀具,其切削工件錶麵粗糙度得到改善。同時,磁化時間及磁化頻率應視為磁化處理中的關鍵調節參數,不同磁化時間及頻率下的W6Mo5Cr4V2高速鋼刀具的切削性能有所不同,在低頻下的效果更好。另外,實驗結果也錶明:經交流磁化處理的W6Mo5Cr4V2高速鋼刀具能夠降低切削過程中的切削力併抑製積屑瘤的產生,從而增加刀具的使用壽命併提高刀具的加工質量。
이용자제적교류자화장치대W6Mo5Cr4V2고속강도구진행료자화처리,병재통용궤상상사용경자화처리적고속강도구급미경자화처리적고속강도구진행료절삭실험,실험결과표명:여보통고속강도구상비,경자화처리후적W6Mo5Cr4V2고속강도구,기절삭공건표면조조도득도개선。동시,자화시간급자화빈솔응시위자화처리중적관건조절삼수,불동자화시간급빈솔하적W6Mo5Cr4V2고속강도구적절삭성능유소불동,재저빈하적효과경호。령외,실험결과야표명:경교류자화처리적W6Mo5Cr4V2고속강도구능구강저절삭과정중적절삭력병억제적설류적산생,종이증가도구적사용수명병제고도구적가공질량。
The W6Mo5Cr4V2 high-speed steel tool was magnetized by the self-made AC magnetization device. Cutting experiments were carried out in a general purpose machine with the magnetized high-speed steel tool and non-magnetized high-speed steel tool. The experimental results indicated that the cutting surface roughness of the workpiece improves by the magnetized W6Mo5Cr4V2 high -speed steel tool. The magnetization time and magnetization frequency should be regarded as key magnetization adjusting parameters. The magnetized W6Mo5Cr4V2 high-speed steel tool show differentiated cutting performances under different magnetization time and frequency. More favorable properties were demonstrated in low frequency. The cutting force could be reduced during the cutting process by using of the magnetized W6Mo5Cr4V2 high-speed steel tool and the formation of the built-up edge in the tool could be inhibited, thereby the tool life was prolonged and the processing quality was improved.