采用粉煤灰、矿渣粉、石灰石粉、硅灰等矿物掺合料，配制出海工自密实高性能混凝土，并重点开展了海工自密实高性能混凝土耐久性，包括抗氯盐侵蚀、碳化、抗冻性和电阻率。试验研究结果表明，6种海工自密实高性能混凝土具有较高的抗氯盐侵蚀性能、抗碳化、抗冻性，56 d 的电通量小于1000 C，90 d 的扩散系数小于1.5×10-12 m2/s，56 d 的碳化深度不大于7.5 mm，56 d抗冻性达到400次循环，56 d 电阻率大于50 kΩ·cm，表现出较高的耐久性和保护钢筋能力。
채용분매회、광사분、석회석분、규회등광물참합료，배제출해공자밀실고성능혼응토，병중점개전료해공자밀실고성능혼응토내구성，포괄항록염침식、탄화、항동성화전조솔。시험연구결과표명，6충해공자밀실고성능혼응토구유교고적항록염침식성능、항탄화、항동성，56 d 적전통량소우1000 C，90 d 적확산계수소우1.5×10-12 m2/s，56 d 적탄화심도불대우7.5 mm，56 d항동성체도400차순배，56 d 전조솔대우50 kΩ·cm，표현출교고적내구성화보호강근능력。
By using fly ash,slag powder,limestone powder,and silica fume,high performance self-compacting concrete for marine structure was mixed and the durability of high performance self-compacting concrete for marine structure was emphatically studied,such as resistance to chloride and carbonization and freeze-thaw,and resistivity.Experimental results showed that the resistance to chloride and carbonization,and resistivity for six kinds of high performance self-compacting concrete for marine structure was high,and charge passed of specimens received standard curing for 28 days was less than 1 000 C,and chloride penetration coefficient of specimens received standard curing for 90 days was less than 1.5×10-12 m2/s,and carbonization depth of specimens received standard curing for 56 days was not more than 7.5 mm,and the freeze-thaw cycle of specimens received standard curing for 56 days reaches 400 times,and the resistivity of specimens received standard curing for 56 days was more than 50 kΩ·cm.In a word,the durability of high performance self-compacting concrete for marine structure developed was high.