主要研究了固相含量与粘度、消泡剂和石膏模对亚氨基二乙酸改性S iC料浆注浆成形坯体密度的影响。结果表明，当料浆固相含量较低、粘度较小时，增大固相含量能提高坯体密度；而当固相含量较高、粘度较大时，降低粘度能有效地提高坯体密度。加入适量合适的消泡剂可适当提高坯体的致密性，同时石膏模的成分和膏水比对坯体密度的影响较大。当半水石膏的两种类型的比例（β/α）为5∶5、膏水比为1．8∶1时，注浆成形坯体密度达最大，为2．5894 g/cm3。
주요연구료고상함량여점도、소포제화석고모대아안기이을산개성S iC료장주장성형배체밀도적영향。결과표명，당료장고상함량교저、점도교소시，증대고상함량능제고배체밀도；이당고상함량교고、점도교대시，강저점도능유효지제고배체밀도。가입괄량합괄적소포제가괄당제고배체적치밀성，동시석고모적성분화고수비대배체밀도적영향교대。당반수석고적량충류형적비례（β/α）위5∶5、고수비위1．8∶1시，주장성형배체밀도체최대，위2．5894 g/cm3。
In this paper ,the effects of solid loading ,viscosity ,defoaming agent and cast on the density of body which was formed by slip casting with iminodiacetic acid coated SiC slurry were studied .The results indicated that increasing solid loading could improve the density of body when the slurry had lower solid loading and viscosity ,and reducing viscosity could improve the density of body when the slurry had higher solid loading and viscosity .It could improve the densification of body through adding some suitable defoaming agent ,and there were some impacts on the density of body that components and the ratio of gypsum powder to water of cast .When semi-hydrated gypsumβ/αwas 5∶5 and the ratio of gypsum pow-der to water was 1 .8∶1 ,the density of body by slip casting achieved biggest and was 2 .589 4 g/cm3 .