采用浸轧的方式，将含有固-液相变材料的调温微胶囊和水性聚氨酯粘合剂的混合溶液处理到纯棉织物上，使织物具备一定的调温效果。通过单因素分析，得出粘合剂和水溶液的最优配比；通过正交实验得出最优浸轧工艺参数。结果表明：粘合剂浓度越大，织物增重越明显；纯棉织物经过整理后透气、透湿性能降低，抗弯刚度变大。在调温整理液配方相同的条件下，轧余率越大，织物增重越明显；当轧余率为110%，烘焙温度为120℃，烘焙时间为5min 时，经调温整理的织物具有较好的耐水洗性能。
채용침알적방식，장함유고-액상변재료적조온미효낭화수성취안지점합제적혼합용액처리도순면직물상，사직물구비일정적조온효과。통과단인소분석，득출점합제화수용액적최우배비；통과정교실험득출최우침알공예삼수。결과표명：점합제농도월대，직물증중월명현；순면직물경과정리후투기、투습성능강저，항만강도변대。재조온정리액배방상동적조건하，알여솔월대，직물증중월명현；당알여솔위110%，홍배온도위120℃，홍배시간위5min 시，경조온정리적직물구유교호적내수세성능。
yurethane (PU) adhesive and thermo-regulating microcapsule containing solid-liquid phase change material so that the fabrics have certain thermo-regulating effect. The optimal ratio of the adhesive and water solution is obtained through single factor analysis and the optimal padding process parameters are obtained through or-thogonal experiment. The result shows that the thicker of the adhesive, the more obvious the fabrics gain weight. The performance of air and moisture permeability is decreased and the bending stiffness is increased when the cotton fabrics have been finished. Under the treating condition of the same thermo-regulating liquid formula, the greater the liquid detention is, the more obvious the fabrics gain weight. When the liquid detention is 110%, the baking temperature is 120℃and the baking time is 5 min, the fabrics prepared by thermal-regu-lating enjoy better washability.