功能材料
功能材料
공능재료
JOURNAL OF FUNCTIONAL MATERIALS
2014年
5期
5074-5078
,共5页
朱胜军%王圣来%丁建旭%刘光霞%王端良%刘琳%顾庆天%许心光
硃勝軍%王聖來%丁建旭%劉光霞%王耑良%劉琳%顧慶天%許心光
주성군%왕골래%정건욱%류광하%왕단량%류림%고경천%허심광
KDP晶体%添加剂%快速生长%溶液稳定性
KDP晶體%添加劑%快速生長%溶液穩定性
KDP정체%첨가제%쾌속생장%용액은정성
KDP crystal%additive%rapid growth%solution stability%crystal defect
在添加不同浓度(0~5×10-3)EDTA 的KDP饱和溶液中,采用“点籽晶”快速生长技术生长了KDP晶体,生长速度约20 mm/d.研究了不同浓度的EDTA对KDP晶体快速生长的影响.实验发现,随着溶液中EDTA添加量的增加,KDP 晶体(100)面的生长速度是先增加经过一个最大值然后减小;晶体宏观外形高宽比则是先减小经过一个最小值然后增加.在溶液中添加适量浓度的EDTA(5×10-5~5×10-4)可以有效地提高生长溶液的稳定性;而过量的添加 ED-TA(>1×10-3)反而会破坏溶液的稳定性,当溶液中EDTA浓度增至5×10-3时,溶液甚至发生“雪崩”,晶体出现母液包藏、添晶和粉碎性裂纹等缺陷.结合KDP的晶体结构和EDTA的分子特点,对其影响机理进行了讨论.
在添加不同濃度(0~5×10-3)EDTA 的KDP飽和溶液中,採用“點籽晶”快速生長技術生長瞭KDP晶體,生長速度約20 mm/d.研究瞭不同濃度的EDTA對KDP晶體快速生長的影響.實驗髮現,隨著溶液中EDTA添加量的增加,KDP 晶體(100)麵的生長速度是先增加經過一箇最大值然後減小;晶體宏觀外形高寬比則是先減小經過一箇最小值然後增加.在溶液中添加適量濃度的EDTA(5×10-5~5×10-4)可以有效地提高生長溶液的穩定性;而過量的添加 ED-TA(>1×10-3)反而會破壞溶液的穩定性,噹溶液中EDTA濃度增至5×10-3時,溶液甚至髮生“雪崩”,晶體齣現母液包藏、添晶和粉碎性裂紋等缺陷.結閤KDP的晶體結構和EDTA的分子特點,對其影響機理進行瞭討論.
재첨가불동농도(0~5×10-3)EDTA 적KDP포화용액중,채용“점자정”쾌속생장기술생장료KDP정체,생장속도약20 mm/d.연구료불동농도적EDTA대KDP정체쾌속생장적영향.실험발현,수착용액중EDTA첨가량적증가,KDP 정체(100)면적생장속도시선증가경과일개최대치연후감소;정체굉관외형고관비칙시선감소경과일개최소치연후증가.재용액중첨가괄량농도적EDTA(5×10-5~5×10-4)가이유효지제고생장용액적은정성;이과량적첨가 ED-TA(>1×10-3)반이회파배용액적은정성,당용액중EDTA농도증지5×10-3시,용액심지발생“설붕”,정체출현모액포장、첨정화분쇄성렬문등결함.결합KDP적정체결구화EDTA적분자특점,대기영향궤리진행료토론.
KDP crystals were grown from aqueous solutions,added with different concentrations of EDTA (0-5×10-3 ),by “point seed”rapid growth technique.The growth rates up to about 20 mm/d.Effects of different concentrations of EDTA-additive on the rapid growth of KDP crystal were investigated.It was found that,with increasing the concentration of EDTA in solution,the growth rate for (100)face of KDP crystal firstly in-creased and then decreased,passing through a maximum;while the aspect ratio of macroscopic shape of these as-grown crystals firstly decreased and then increased,passing through a minimum.Appropriate amount of ED-TA (5×10-5-5×10-4)doped in growth solution enhanced the stability of growth solution,but excess addition of EDTA (>1 × 1 0-3 )had the adverse effect.When the concentration of EDTA in solution increased to 5 × 10-3 ,“avalanche”even occurred in solution and many macro defects of crystal appeared,such as mother liquid inclusions,parasite crystals and crushing cracks.The impact mechanism was also analyzed combining with the structure of KDP crystal and chemical characteristic of EDTA molecule.