CHINESE JOURNAL OF CHEMICAL ENGINEERING
2014年
5期
590-595
,共6页
肖政伟%胡国荣%杜柯%彭忠东
肖政偉%鬍國榮%杜柯%彭忠東
초정위%호국영%두가%팽충동
lithium ion cell%reduced iron powder%ball-milling%LiFePO4/C%nano-sized primary particle
A facile and practical route was introduced to prepare LiFePO4/C cathode material with nano-sized primary particles and excellent electrochemical performance. LiH2PO4 was synthesized by using H3PO4 and LiOH as raw materials. Then, as-prepared LiH2PO4, reduced iron powder andα-D-glucose were ball-milled, dried and sin-tered to prepare LiFePO4/C. X-ray diffractometry was used to characterize LiH2PO4, ball-milled product and LiFePO4/C. Differential scanning calorimeter-thermo gravimetric analysis was applied to investigate possible reac-tions in sintering and find suitable temperature for LiFePO4 formation. Scanning electron microscopy was em-ployed for the morphology of LiFePO4/C. As-prepared LiH2PO4 is characterized to be in P21cn(33) space group, which reacts with reduced iron powder to form Li3PO4, Fe3(PO4)2 and H2 in ball-milling and sintering. The appro-priate temperature for LiFePO4/C synthesis is 541.3-976.7 °C. LiFePO4/C prepared at 700 °C presents nano-sized primary particles forming aggregates. Charge-discharge examination indicates that as-prepared LiFePO4/C displays appreciable discharge capacities of 145 and 131 mA·h·g-1 at 0.1 and 1 C respectively and excellent discharge ca-pacity retention.