利用相转移法,通过控制溶剂蒸发温度制备了不同孔隙结构的聚酰胺(PA)多孔膜,用扫描电镜(SEM)和材料力学试验机对不同孔隙结构的PA多孔膜的形貌和力学性能进行了表征.将PA 多孔膜与类成骨细胞(MG63)共培养来考察不同孔隙结构多孔膜的细胞生物学响应.结果表明,随着溶剂蒸发温度升高,制备的PA多孔膜孔径大小逐渐增大,在40℃下制备的多孔膜孔隙结构均匀,孔径为10~20μm,其弹性模量与拉伸强度分别达到(20.2±0.9)和(5.2±0.5)MPa.细胞实验表明,与40℃下制备的PA多孔膜共培养后,细胞在其表面伸展爬行,形态结构完整,增殖明显.具有可控特性的 PA 多孔膜能够满足其在骨组织引导再生临床中的应用.
利用相轉移法,通過控製溶劑蒸髮溫度製備瞭不同孔隙結構的聚酰胺(PA)多孔膜,用掃描電鏡(SEM)和材料力學試驗機對不同孔隙結構的PA多孔膜的形貌和力學性能進行瞭錶徵.將PA 多孔膜與類成骨細胞(MG63)共培養來攷察不同孔隙結構多孔膜的細胞生物學響應.結果錶明,隨著溶劑蒸髮溫度升高,製備的PA多孔膜孔徑大小逐漸增大,在40℃下製備的多孔膜孔隙結構均勻,孔徑為10~20μm,其彈性模量與拉伸彊度分彆達到(20.2±0.9)和(5.2±0.5)MPa.細胞實驗錶明,與40℃下製備的PA多孔膜共培養後,細胞在其錶麵伸展爬行,形態結構完整,增殖明顯.具有可控特性的 PA 多孔膜能夠滿足其在骨組織引導再生臨床中的應用.
이용상전이법,통과공제용제증발온도제비료불동공극결구적취선알(PA)다공막,용소묘전경(SEM)화재료역학시험궤대불동공극결구적PA다공막적형모화역학성능진행료표정.장PA 다공막여류성골세포(MG63)공배양래고찰불동공극결구다공막적세포생물학향응.결과표명,수착용제증발온도승고,제비적PA다공막공경대소축점증대,재40℃하제비적다공막공극결구균균,공경위10~20μm,기탄성모량여랍신강도분별체도(20.2±0.9)화(5.2±0.5)MPa.세포실험표명,여40℃하제비적PA다공막공배양후,세포재기표면신전파행,형태결구완정,증식명현.구유가공특성적 PA 다공막능구만족기재골조직인도재생림상중적응용.
The porous polyamide (PA)membranes with different structure were prepared using phase-inversion technique by controlling the temperature of solvent evaporation.The morphologies and mechanical properties of the porous membrane were characterized by SEM and universal mechanical testing machine.The cytological properties of the porous membranes were studied in vitro by co-cultured with osteoblast-like MG63 cells.The results showed that the pore size of the PA membranes was increasing with the increasing of the treatment tem-perature.The uniform pores was obtained and the average pore size was 10 to 20μm when heated at 40 ℃.The elastic modulus and tensile strength reach (20.2±0.9)and (5.2±0.5)MPa,respectively.The cytological exper-iments demonstrated that the porous membranes displayed favorable cytocompatibility.After co-cultured with the PA membranes prepared at 40 ℃,porous membranes acted as a good matrix for MG63 adhesion,crawl and proliferation.The cytocompatibility,tunable mechanical properties,hydrophilicity of the porous membranes cauld meet the requirement of guided bone regeneration.