刘波%贺跃辉%夏宁%彭博%邹应萍
劉波%賀躍輝%夏寧%彭博%鄒應萍
류파%하약휘%하저%팽박%추응평
窄带隙%Pechmann类聚合物%合成%光伏应用
窄帶隙%Pechmann類聚閤物%閤成%光伏應用
착대극%Pechmann류취합물%합성%광복응용
low bandgap%Pechmann-based copolymer%synthesis%photovoltaic application
通过Stille偶联聚合方法合成一种新型的Pechmann类窄带隙聚合物(PBDTTP),并将其应用到太阳能电池的研究中。PBDTTP具有高的相对分子质量、良好的溶解性能与成膜性能。紫外-可见吸收光谱表明,在薄膜状态下,PBDTTP的吸收范围在300~900 nm 之间,其最大吸收峰位置在748 nm,相应的光学带隙为1.37 eV。光伏器件的结构为(ITO)/PEDOT:PSS/PBDTTP:PC71BM/Al,初步的器件结果显示,当PBDTTP与PC71BM质量比为1:2时,光伏器件具有最高的能量转换效率(PCE),为1.03%,对应的开路电压(Voc)为0.75 V,短路电流密度(Jsc)为2.24 mA/cm2,填充因子(FF)为61.2%。
通過Stille偶聯聚閤方法閤成一種新型的Pechmann類窄帶隙聚閤物(PBDTTP),併將其應用到太暘能電池的研究中。PBDTTP具有高的相對分子質量、良好的溶解性能與成膜性能。紫外-可見吸收光譜錶明,在薄膜狀態下,PBDTTP的吸收範圍在300~900 nm 之間,其最大吸收峰位置在748 nm,相應的光學帶隙為1.37 eV。光伏器件的結構為(ITO)/PEDOT:PSS/PBDTTP:PC71BM/Al,初步的器件結果顯示,噹PBDTTP與PC71BM質量比為1:2時,光伏器件具有最高的能量轉換效率(PCE),為1.03%,對應的開路電壓(Voc)為0.75 V,短路電流密度(Jsc)為2.24 mA/cm2,填充因子(FF)為61.2%。
통과Stille우련취합방법합성일충신형적Pechmann류착대극취합물(PBDTTP),병장기응용도태양능전지적연구중。PBDTTP구유고적상대분자질량、량호적용해성능여성막성능。자외-가견흡수광보표명,재박막상태하,PBDTTP적흡수범위재300~900 nm 지간,기최대흡수봉위치재748 nm,상응적광학대극위1.37 eV。광복기건적결구위(ITO)/PEDOT:PSS/PBDTTP:PC71BM/Al,초보적기건결과현시,당PBDTTP여PC71BM질량비위1:2시,광복기건구유최고적능량전환효솔(PCE),위1.03%,대응적개로전압(Voc)위0.75 V,단로전류밀도(Jsc)위2.24 mA/cm2,전충인자(FF)위61.2%。
A new low bandgap Pechmann-based polymer (PBDTTP) was synthesized, and this is the first time to make Pechmann-based polymer for photovoltaic applications. PBDTTP was found to be soluble in common organic solvents, with excellent film forming properties. The gel permeation chromatography (GPC) shows that the polymer has relatively high relative molecular mass. The polymer film exhibits broad absorption band in the wavelength region from 300 to 900 nm with an optical bandgap of 1.37 eV. Preliminary photovoltaic cells based on the composite structure of ITO/PEDOT:PSS/PBDTTP:PC71BM/Al show an open-circuit voltage Voc of 0.75 V, a power conversion efficiency (PCE) of 1.03%, a short circuit current density (Jsc) of 2.24 mA/cm2 and a fill factor of 61.2%.