李权%彭建%程仁菊%刘文君%曾斌%蒋显全%潘复生
李權%彭建%程仁菊%劉文君%曾斌%蔣顯全%潘複生
리권%팽건%정인국%류문군%증빈%장현전%반복생
镁合金%均匀化%显微组织%挤压
鎂閤金%均勻化%顯微組織%擠壓
미합금%균균화%현미조직%제압
magnesium alloy%homogenization%microstructure%extrusion
研究不同含量的稀土元素 Ce对 ZK20镁合金组织、力学性能以及热变形行为的影响,通过采用常规金相、X 射线、SEM、XRD 分析,以及常温拉伸和热模拟压缩实验,分析 Ce元素在 ZK20镁合金中的存在形式及其对合金组织和性能的作用机制。结果表明,在实验范围内(0~0.68%Ce(质量分数,下同)),随着Ce的添加,合金中出现的含Ce合金相τ相不断增多,形态向不连续网状及网状转变,合金经热挤压后,Ce元素能改善合金的再结晶程度,晶粒尺寸随Ce添加量的增加不断变小,其中Ce添加量为0.7%的合金挤压态力学性能最佳,其室温抗拉强度为261 MPa,屈服强度为198 MPa,延伸率为24.6%。280℃×4 h的退火工艺能使挤压态合金的强度和塑性提高,其抗拉强度达到272 MPa,屈服强度达到209 MPa,延伸率为26%。Ce的加入能使 ZK20合金由脆性断裂向部分韧窝的混合断裂转变。
研究不同含量的稀土元素 Ce對 ZK20鎂閤金組織、力學性能以及熱變形行為的影響,通過採用常規金相、X 射線、SEM、XRD 分析,以及常溫拉伸和熱模擬壓縮實驗,分析 Ce元素在 ZK20鎂閤金中的存在形式及其對閤金組織和性能的作用機製。結果錶明,在實驗範圍內(0~0.68%Ce(質量分數,下同)),隨著Ce的添加,閤金中齣現的含Ce閤金相τ相不斷增多,形態嚮不連續網狀及網狀轉變,閤金經熱擠壓後,Ce元素能改善閤金的再結晶程度,晶粒呎吋隨Ce添加量的增加不斷變小,其中Ce添加量為0.7%的閤金擠壓態力學性能最佳,其室溫抗拉彊度為261 MPa,屈服彊度為198 MPa,延伸率為24.6%。280℃×4 h的退火工藝能使擠壓態閤金的彊度和塑性提高,其抗拉彊度達到272 MPa,屈服彊度達到209 MPa,延伸率為26%。Ce的加入能使 ZK20閤金由脆性斷裂嚮部分韌窩的混閤斷裂轉變。
연구불동함량적희토원소 Ce대 ZK20미합금조직、역학성능이급열변형행위적영향,통과채용상규금상、X 사선、SEM、XRD 분석,이급상온랍신화열모의압축실험,분석 Ce원소재 ZK20미합금중적존재형식급기대합금조직화성능적작용궤제。결과표명,재실험범위내(0~0.68%Ce(질량분수,하동)),수착Ce적첨가,합금중출현적함Ce합금상τ상불단증다,형태향불련속망상급망상전변,합금경열제압후,Ce원소능개선합금적재결정정도,정립척촌수Ce첨가량적증가불단변소,기중Ce첨가량위0.7%적합금제압태역학성능최가,기실온항랍강도위261 MPa,굴복강도위198 MPa,연신솔위24.6%。280℃×4 h적퇴화공예능사제압태합금적강도화소성제고,기항랍강도체도272 MPa,굴복강도체도209 MPa,연신솔위26%。Ce적가입능사 ZK20합금유취성단렬향부분인와적혼합단렬전변。
The effects of different Ce contents on the microstructure,mechanical properties and performance of hot deformation were investigated.By methods of OM,X-ray,SEM,XRD,tensile test at room temperature and hot compression test on Gleeble 1500D thermal-mechanical simulator,the mechanism properties of Ce ele-ment in ZK20 and its effect on microstructure were analyzed.The results showed that within the experimental range (0 to 0.68% Ce (mass fraction,the same below)),the phaseτwere increased with the addition of Ce, the form were changed to the discontinuity mesh and mesh in the alloy by hot extrusion.Ce element could im-prove the recrystallization of the alloy.The grain size continuously decreased with increasing Ce.The extruded alloy exhibted best mechanical properties with the 0.7% addition of Ce.Its room temperature tensile strength was 261 MPa,yield strength was 198 MPa,elongation was 24.6%.Annealing process in condition of 280 ℃and 4 h could contribute to the strength and ductility of the alloy.Its tensile strength was improved to 272 MPa,yield strength was improved to 209 MPa,and elongation was 26%.The addition of Ce into ZK20 alloy could cause the transition of brittle fracture to brittle and dimple mixed fracture.