OLED%Au%微腔效应%光透过率%色纯度
OLED%Au%微腔效應%光透過率%色純度
OLED%Au%미강효응%광투과솔%색순도
OLED%Au%Microcavity effect%Light transmittance%Color purity
在一些有机电致发光器件中,A u常被用作阳极,研究者希望A u在导电的同时兼具半透明可出光的属性,这要求Au在能导电的同时厚度要尽量薄。因此制备两种金属共同组成电极成为了选择。将半透明Au/Al层插入阳极一侧,制备了结构为 ITO/Al(16 nm)/Au(10 nm)/TPD(30 nm)/AlQ(30 nm)/LiF(0.5 nm)/Al的OLED器件,相对于器件ITO/TPD(30 nm)/AlQ(30 nm)/LiF(0.5 nm)/Al在长波方向出现了光谱窄化现象,通过分析和实验判断该现象是Au薄膜特有的对光的选择透过性造成,而并非微腔效应。阳极一侧加入了Au/Al的器件保持了广视角无角度依赖的优点,同时可以输出滤掉部分红光的纯度更高的发光,发光色纯度得到了改善。
在一些有機電緻髮光器件中,A u常被用作暘極,研究者希望A u在導電的同時兼具半透明可齣光的屬性,這要求Au在能導電的同時厚度要儘量薄。因此製備兩種金屬共同組成電極成為瞭選擇。將半透明Au/Al層插入暘極一側,製備瞭結構為 ITO/Al(16 nm)/Au(10 nm)/TPD(30 nm)/AlQ(30 nm)/LiF(0.5 nm)/Al的OLED器件,相對于器件ITO/TPD(30 nm)/AlQ(30 nm)/LiF(0.5 nm)/Al在長波方嚮齣現瞭光譜窄化現象,通過分析和實驗判斷該現象是Au薄膜特有的對光的選擇透過性造成,而併非微腔效應。暘極一側加入瞭Au/Al的器件保持瞭廣視角無角度依賴的優點,同時可以輸齣濾掉部分紅光的純度更高的髮光,髮光色純度得到瞭改善。
재일사유궤전치발광기건중,A u상피용작양겁,연구자희망A u재도전적동시겸구반투명가출광적속성,저요구Au재능도전적동시후도요진량박。인차제비량충금속공동조성전겁성위료선택。장반투명Au/Al층삽입양겁일측,제비료결구위 ITO/Al(16 nm)/Au(10 nm)/TPD(30 nm)/AlQ(30 nm)/LiF(0.5 nm)/Al적OLED기건,상대우기건ITO/TPD(30 nm)/AlQ(30 nm)/LiF(0.5 nm)/Al재장파방향출현료광보착화현상,통과분석화실험판단해현상시Au박막특유적대광적선택투과성조성,이병비미강효응。양겁일측가입료Au/Al적기건보지료엄시각무각도의뢰적우점,동시가이수출려도부분홍광적순도경고적발광,발광색순도득도료개선。
Au was used as anode in some kind of organic electroluminescent devices .Sometimes transparent Au electrodes are re-quired ,which means that the thickness of Au electrode should be as thin as possible .Therefore ,two metals together forming an electrode become a choice .In the present paper ,translucent Au/Al layer was inserted to anode side ,and OLED device with the structure of ITO/Al (16 nm)/Au (10 nm)/TPD (30 nm)/AlQ (30 nm)/LiF(0.5 nm)/Al was prepared .There is a spectral narrowing phenomenon on the device ITO/TPD (30 nm)/AlQ (30 nm)/LiF (0.5 nm)/Al ,and through analysis and experiment it was found that this phenomenon comes from selective permeability to light of Au thin film rather than the microcavity effect . The device maintains wide viewing angle ,without the angular dependence .And the color purity of device with Au thin film is improved .