针对某大型圆柱形工件,利用Ni60AA合金粉末,采用高频感应重熔工艺,在工件表面制备了合金涂层,并对涂层的组织进行了分析并测试了涂层的硬度和耐磨性。结果表明,感应熔涂制备的涂层与基体形成了良好的冶金结合,涂层与基体之间存在明显的"白亮带",涂层基体中分布着丰富的硬质相,显著提高了涂层的硬度,具有良好的耐磨性。
針對某大型圓柱形工件,利用Ni60AA閤金粉末,採用高頻感應重鎔工藝,在工件錶麵製備瞭閤金塗層,併對塗層的組織進行瞭分析併測試瞭塗層的硬度和耐磨性。結果錶明,感應鎔塗製備的塗層與基體形成瞭良好的冶金結閤,塗層與基體之間存在明顯的"白亮帶",塗層基體中分佈著豐富的硬質相,顯著提高瞭塗層的硬度,具有良好的耐磨性。
침대모대형원주형공건,이용Ni60AA합금분말,채용고빈감응중용공예,재공건표면제비료합금도층,병대도층적조직진행료분석병측시료도층적경도화내마성。결과표명,감응용도제비적도층여기체형성료량호적야금결합,도층여기체지간존재명현적"백량대",도층기체중분포착봉부적경질상,현저제고료도층적경도,구유량호적내마성。
A large cylindrical work piece,using Ni60AA alloy powder, with high-frequency induction melting process, prepared in the surface Ni-based self-fluxing alloy coating, and coating and phase structure was analyzed and tested the coating hardness and wear resistance. The results show that the induction cladding Ni-based coatings prepared with the basic shape has become a good metallurgical bonding between coating and substrate obvious "white-band", Ni coating distribution in the matrix rich hard phase, significantly increased hardness of the coating has good wear resistance.