以漆酚为基体,铜为导电填料,利用紫外光固化法制备漆酚/铜复合导电涂料,讨论了涂膜中铜的含量对漆膜导电性能的影响,并测试了漆膜的常规物理机械性能和耐化学腐蚀性能。结果表明,在紫外光辐照下,漆酚/铜混合物涂膜可快速固化。当铜含量达到45%(wt%)时,漆膜的表面电阻率为13.1Ω·cm,耐冲击强度50kg·cm。
以漆酚為基體,銅為導電填料,利用紫外光固化法製備漆酚/銅複閤導電塗料,討論瞭塗膜中銅的含量對漆膜導電性能的影響,併測試瞭漆膜的常規物理機械性能和耐化學腐蝕性能。結果錶明,在紫外光輻照下,漆酚/銅混閤物塗膜可快速固化。噹銅含量達到45%(wt%)時,漆膜的錶麵電阻率為13.1Ω·cm,耐遲擊彊度50kg·cm。
이칠분위기체,동위도전전료,이용자외광고화법제비칠분/동복합도전도료,토론료도막중동적함량대칠막도전성능적영향,병측시료칠막적상규물리궤계성능화내화학부식성능。결과표명,재자외광복조하,칠분/동혼합물도막가쾌속고화。당동함량체도45%(wt%)시,칠막적표면전조솔위13.1Ω·cm,내충격강도50kg·cm。
The polyurushiol/copper composite conductive coating was prepared by UV irradiation and the effect of concentration of copper on the electrical resistivity of the composite film was studied. The physico - mechanical properties and the chemical resistance properties of the polyurushiol/copper composite film were also discussed. The results show that the polyurushiol/copper composite film was cured by UV irradiation in 2 rain. The surface resistivity value is 13.1Ω·cm and the impact strength is 50kg· cm when the concentration of copper is 45% (wt%).