为了研究304不锈钢光纤激光-MIG（metal inert-gas welding）复合焊接性能，采用正离焦的方法进行了大量的焊接实验。分析了送丝速率、弧长、激光功率、光丝距离、焊接方向和不同对接接头等参量对焊接成形的影响。结果表明，在焊丝的干伸长度为15mm、光丝距离为2mm、采用前送丝时，通过适当调节送丝速率、弧长可以实现较好的焊接效果；小直径焊丝有利于形成较小熔宽和余高的焊缝，而通过加入引弧板可以解决初始位置焊缝成形较差的问题。因此，采用合适的激光-MIG复合焊接工艺可以实现304不锈钢较好的焊接效果。
위료연구304불수강광섬격광-MIG（metal inert-gas welding）복합한접성능，채용정리초적방법진행료대량적한접실험。분석료송사속솔、호장、격광공솔、광사거리、한접방향화불동대접접두등삼량대한접성형적영향。결과표명，재한사적간신장도위15mm、광사거리위2mm、채용전송사시，통과괄당조절송사속솔、호장가이실현교호적한접효과；소직경한사유리우형성교소용관화여고적한봉，이통과가입인호판가이해결초시위치한봉성형교차적문제。인차，채용합괄적격광-MIG복합한접공예가이실현304불수강교호적한접효과。
By adopting the positive defocusing amount , the effect of fiber laser-metal inert-gas welding ( MIG) hybrid welding parameters on the weld morphology of 304 stainless steel, mainly including wire feeding speed , arc length, laser power, the distance between laser and MIG arc , welding direction and butt joint , was studied through many welding experiments.Results indicate that the good welding effects can be obtained by matching proper wire feeding speed and arc length when the extension length is 15mm and the distance between laser and MIG is 2mm.The results also show that small diameter wire will help to make the narrow weld width and low weld reinforcement , end tab will solve the problem of bad welding morphology at welding initial position .A conclusion is drawn that good welding quality of 304 stainless steel can be achieved when the proper welding procedure of laser-MIG hybrid welding is adopted .