贵金属
貴金屬
귀금속
PRECIOUS METALS
2013年
2期
15-19
,共5页
吴保安%刘庆宾%陈德茂%汪建胜%唐会毅%陈小军
吳保安%劉慶賓%陳德茂%汪建勝%唐會毅%陳小軍
오보안%류경빈%진덕무%왕건성%당회의%진소군
金属材料%热电偶%Pt-Rh合金%电阻率%抗拉强度%硬度
金屬材料%熱電偶%Pt-Rh閤金%電阻率%抗拉彊度%硬度
금속재료%열전우%Pt-Rh합금%전조솔%항랍강도%경도
metal materials%thermocouple%Pt-Rh alloy%resistivity%tensile strength%hardness
PtRh40/PtRh20高温热电偶长期使用温度为1750℃,主要用于飞机尾焰高温测量,属于非标热电偶,目前国内主要依靠进口。研究了 PtRh40、PtRh20退火温度与合金电阻率、抗拉强度及加工率与抗拉强度、硬度的关系,并测试了PtRh40/PtRh20热电偶热电性能。结果表明:抗拉强度随退火温度的升高先升高再急剧下降,最后稳定在一个平台,两者大约在900℃时抗拉强度降至最低;电阻率均随退火温度升高而升高;抗拉强度与硬度均随加工率的增加而提高;PtRh40/PtRh20配对热电势相对ASTM E1751-2000标准热电势测试结果为在1200℃时误差为1℃,在1500℃时误差2℃,在1700℃时误差1℃。
PtRh40/PtRh20高溫熱電偶長期使用溫度為1750℃,主要用于飛機尾燄高溫測量,屬于非標熱電偶,目前國內主要依靠進口。研究瞭 PtRh40、PtRh20退火溫度與閤金電阻率、抗拉彊度及加工率與抗拉彊度、硬度的關繫,併測試瞭PtRh40/PtRh20熱電偶熱電性能。結果錶明:抗拉彊度隨退火溫度的升高先升高再急劇下降,最後穩定在一箇平檯,兩者大約在900℃時抗拉彊度降至最低;電阻率均隨退火溫度升高而升高;抗拉彊度與硬度均隨加工率的增加而提高;PtRh40/PtRh20配對熱電勢相對ASTM E1751-2000標準熱電勢測試結果為在1200℃時誤差為1℃,在1500℃時誤差2℃,在1700℃時誤差1℃。
PtRh40/PtRh20고온열전우장기사용온도위1750℃,주요용우비궤미염고온측량,속우비표열전우,목전국내주요의고진구。연구료 PtRh40、PtRh20퇴화온도여합금전조솔、항랍강도급가공솔여항랍강도、경도적관계,병측시료PtRh40/PtRh20열전우열전성능。결과표명:항랍강도수퇴화온도적승고선승고재급극하강,최후은정재일개평태,량자대약재900℃시항랍강도강지최저;전조솔균수퇴화온도승고이승고;항랍강도여경도균수가공솔적증가이제고;PtRh40/PtRh20배대열전세상대ASTM E1751-2000표준열전세측시결과위재1200℃시오차위1℃,재1500℃시오차2℃,재1700℃시오차1℃。
The long-term using temperature of PtRh40/PtRh20 high-temperature thermocouple wire is 1750℃. PtRh40/PtRh20 is belong to non-standard thermocouple, and mainly applies to measure the aircraft efflux plasma temperature. The influences of annealing temperature on the tensile strength and resistivity of PtRh40 and PtRh20 alloy wires, and the influences of the cold working on tensile strength and vickers hardness of the wires were studied. The results indicated that the tensile strengths increased with the increase of annealing temperature at first, then decreased sharply, finally it is stable forming a platform. The resistivities were increased with the annealing temperature, and the tensile strength and hardness were increased with the cold working. The errors of matching thermoelectric potential of PtRh40- PtRh20 relative to ASTM E1751-2000 standard thermoelectric power is 1℃ at 1200℃, 2℃ at 1500℃, and 1℃ at 1700℃.