研究了以新型硅酸钙填料与阻燃剂三氧化二锑和十溴二苯乙烷协同作用，通过纸张表面涂布法制备阻燃箱纸板。对涂布原纸中淀粉的用量、涂布原纸中硅酸钙填料添加量、两种阻燃剂的配比、涂料中硅酸钙填料使用量以及涂布量进行实验。阻燃纸以淀粉用量为1.0%、原纸中硅酸钙填料添加量10%、三氧化二锑与十溴二苯乙烷配比为2∶1、涂料中硅酸钙填料用量为10%、涂布量为30g/m2为实验条件时，达到物理强度和阻燃性能的较好组合。
연구료이신형규산개전료여조연제삼양화이제화십추이분을완협동작용，통과지장표면도포법제비조연상지판。대도포원지중정분적용량、도포원지중규산개전료첨가량、량충조연제적배비、도료중규산개전료사용량이급도포량진행실험。조연지이정분용량위1.0%、원지중규산개전료첨가량10%、삼양화이제여십추이분을완배비위2∶1、도료중규산개전료용량위10%、도포량위30g/m2위실험조건시，체도물리강도화조연성능적교호조합。
A study on a filler of novel calcium silicate working with antimony trioxide and decabromodiphenyl ethane synergy was explored for preparation of flame-retardant paper cardboard by coating. It was found that flame-retardant paper can get a good physical strength and a good effect of lfame-retardant with conditions of the amount of 1.0%starch in pulp, dosage of calcium silicate ifller of 10%added in base paper, antimony trioxide and decabromodiphenyl ethane ratio of 2 to 1 and dosage of 10%calcium silicate ifller in coating color and 30g/m2 coating weight.