刘长淼%吴东印%王守敬%吕子虎%赵登魁%卫敏%冯安生%郭珍旭
劉長淼%吳東印%王守敬%呂子虎%趙登魁%衛敏%馮安生%郭珍旭
류장묘%오동인%왕수경%려자호%조등괴%위민%풍안생%곽진욱
钛磁铁矿%磁选%磁筛
鈦磁鐵礦%磁選%磁篩
태자철광%자선%자사
titanium magnetite%magnetic separating%magnetic-screen separator
云南安益钛磁铁矿储量巨大,工业开发利用价值巨大。通过工艺矿物学研究可知,原矿主要含铁矿物为钛磁铁矿和钛铁矿,主要脉石矿物为辉石和斜长石,钛磁铁矿的嵌布粒度相对较粗。实验室小型试验采用“弱磁粗选-磁筛精选”流程,控制磨矿细度为-0.074mm 含量50%,控制弱磁磁场强度在100~170kA/m区间内,磁筛间距控制为70mm,可获得TFe 品位55.85%、回收率为59.16%的钛磁铁矿精矿。扩大连续试验时,控制磨矿细度为-0.074mm 含量50%,一段磁选的磁场强度控制为143.31KA/m,磁筛间距控制为70mm,可获得 TFe 品位53.89%、TiO2品位13.35%,TFe 回收率为62.24%、TiO2回收率为51.69%的精矿。
雲南安益鈦磁鐵礦儲量巨大,工業開髮利用價值巨大。通過工藝礦物學研究可知,原礦主要含鐵礦物為鈦磁鐵礦和鈦鐵礦,主要脈石礦物為輝石和斜長石,鈦磁鐵礦的嵌佈粒度相對較粗。實驗室小型試驗採用“弱磁粗選-磁篩精選”流程,控製磨礦細度為-0.074mm 含量50%,控製弱磁磁場彊度在100~170kA/m區間內,磁篩間距控製為70mm,可穫得TFe 品位55.85%、迴收率為59.16%的鈦磁鐵礦精礦。擴大連續試驗時,控製磨礦細度為-0.074mm 含量50%,一段磁選的磁場彊度控製為143.31KA/m,磁篩間距控製為70mm,可穫得 TFe 品位53.89%、TiO2品位13.35%,TFe 迴收率為62.24%、TiO2迴收率為51.69%的精礦。
운남안익태자철광저량거대,공업개발이용개치거대。통과공예광물학연구가지,원광주요함철광물위태자철광화태철광,주요맥석광물위휘석화사장석,태자철광적감포립도상대교조。실험실소형시험채용“약자조선-자사정선”류정,공제마광세도위-0.074mm 함량50%,공제약자자장강도재100~170kA/m구간내,자사간거공제위70mm,가획득TFe 품위55.85%、회수솔위59.16%적태자철광정광。확대련속시험시,공제마광세도위-0.074mm 함량50%,일단자선적자장강도공제위143.31KA/m,자사간거공제위70mm,가획득 TFe 품위53.89%、TiO2품위13.35%,TFe 회수솔위62.24%、TiO2회수솔위51.69%적정광。
An-Yi mine has very large reserves of titanic magnetite,and is of enormous industrial values.On the basis of technological mineralogy,iron minerals were mainly titanic magnetite and ilmenite, and gangue minerals were mostly pyroxene and plagioclase.The dissemination size of titanic magnetite particles was rough and large.Couples of bench tests were carried out by the process of“roughing by weak-magnetic and concentrating by magnetic-screen separator”.While the content of -0.074mm fraction in grinding output was 50%,magnetic intensity of roughing was controlled in the section of 100-170KA/m, and the distance of magnetic screen was 70mm,a good concentration indexes were gained with TFe grade of 55.85% and recovery rate of 59.16%.And conditions of pilot test were same as that of bench test,expect the roughing magnetic intensity was adjusted to 143.31kA/m,and final concentrate was obtained with the TFe and TiO2 grade of 53.89% and 13.35%,and TFe and TiO2 recovery rate of 62.24% and 51.69%.