制备了LCD用ODF框胶，采用FTIR-ATR和测定凝胶含量的方法分析了框胶的UV固化速度以及固化程度。采用SEM对ODF框胶中填料的分散状态进行了分析，对ODF框胶的粘接性能进行了考2查。结果表明，在UV固化能量达到1500 mJ/cm时即可固化完全，凝胶含量达到99.88%。添加到框胶体系中的有机硅微粉和白炭黑分散均匀，无团聚颗粒存在；ODF框胶对玻璃的粘接强度较高，达到17.90 MPa，经过水煮老化处理后对玻璃的粘接强度仍达到15.12 MPa。
제비료LCD용ODF광효，채용FTIR-ATR화측정응효함량적방법분석료광효적UV고화속도이급고화정도。채용SEM대ODF광효중전료적분산상태진행료분석，대ODF광효적점접성능진행료고2사。결과표명，재UV고화능량체도1500 mJ/cm시즉가고화완전，응효함량체도99.88%。첨가도광효체계중적유궤규미분화백탄흑분산균균，무단취과립존재；ODF광효대파리적점접강도교고，체도17.90 MPa，경과수자노화처리후대파리적점접강도잉체도15.12 MPa。
The ODF seal for LCD was prepared.The curing rate and degree of cure were analyzed by FTIR-ATR and gel fraction.The dispersion of fillers was characterized by SEM,and the adhesive properties of ODF seal were 2investigated.The results show that the seal has completely cured at 1500mJ/cm ,and the gel fraction was 99.88%.The silicone powder and silica-gel filler were well-dispersed in the seal without any agglomerated particles.The bonding strength of the ODF seal was high,which was 17.90 MPa,and after boiling water ageing the bonding strength of the ODF seal was 15.12MPa.