以 Fe73.5 Cu1 Nb3 Si13.5 B9粉体为复合相,硅橡胶为基体,制得粉体含量为83%(质量分数)、厚度200μm的复合薄膜；采用 TH2816LCR 数字电桥测试频率1kHz下薄膜的阻抗Z 随压应力σ的变化情况,用LYYL-500N高档型微机控制压力试验机对薄膜体系进行程序控制加载；薄膜采用电容方式连接。研究了复合薄膜在压应力连续加载/卸载和压应力保持加载/卸载状况下的力敏特性。研究表明,复合薄膜在连续加载/卸载速度≤0.5mm/min 和保压加载/卸载条件下,当测试频率1kHz、压应力0.2~1.0MPa 时,具有良好的力敏稳定性和灵敏性。随着应力σ增大,阻抗Z 呈非线性下降,SI%值为6%~23%,灵敏精度k值为2~0.2,测试标准偏差稳定在0.02~0.05,薄膜对于<0.3MPa应力更加灵敏。增加测试频率可以提高薄膜体系的力敏灵敏度。在压应力0.2~1.0MPa范围内,薄膜弹性后效现象显著,导致薄膜加载Z-σ曲线与卸载曲线不重合。
이 Fe73.5 Cu1 Nb3 Si13.5 B9분체위복합상,규상효위기체,제득분체함량위83%(질량분수)、후도200μm적복합박막；채용 TH2816LCR 수자전교측시빈솔1kHz하박막적조항Z 수압응력σ적변화정황,용LYYL-500N고당형미궤공제압력시험궤대박막체계진행정서공제가재；박막채용전용방식련접。연구료복합박막재압응력련속가재/사재화압응력보지가재/사재상황하적력민특성。연구표명,복합박막재련속가재/사재속도≤0.5mm/min 화보압가재/사재조건하,당측시빈솔1kHz、압응력0.2~1.0MPa 시,구유량호적력민은정성화령민성。수착응력σ증대,조항Z 정비선성하강,SI%치위6%~23%,령민정도k치위2~0.2,측시표준편차은정재0.02~0.05,박막대우<0.3MPa응력경가령민。증가측시빈솔가이제고박막체계적력민령민도。재압응력0.2~1.0MPa범위내,박막탄성후효현상현저,도치박막가재Z-σ곡선여사재곡선불중합。
Composite film was prepared by Fe73.5 Cu1 Nb3 Si13.5 B9 powder as compound phase and silicone rubber as matrix phase.The content of powder was 83% and the thickness of film was 200μm.Impedance-Z and stress-σof film were tested by TH2816LCR digital bridge when frequency was 1kHz.LYYL-500N high-grade type microcomputer control pressure testing machine was used to program control loading.Film system was con-nected by capacitance way,the force-sensitive properties were studied when stress loading and unloading was continuous or retentive.The results show that when frequency was 1kHz and stress was 0.2-1.0MPa,compos-ite film has excellent force-sensitive stability and sensitivity in condition that the speed of continuous loading and unloading was low 0.5mm/mim and loading and unloading was retentive.The impedance was declining nonlin-ear with the stress was increasing.The value of SI% was 6%-23%,the value of sensitivity-k was 2-0.2,the standard deviation was stability in 0.02-0.05.The film was more sensitive when stress was low to 0.3MPa.In-creasing test frequency can improve the sensitivity of film.When stress was between 0.2-1.0MPa the elastic af-tereffect phenomenon was obvious,which leads to the loading Z-σcurve and unloading was not coincident.