CVI processes of different diameter of preforms were studied in this research to analyze the influence of the scale of perform to the densification in CVI.Preforms of the equivalent height of 90mm and each diame-ter was 60,120 and 180mm was used to simulate the porosity and density field in 4 periods.Results showed that it was easy to get uniform and high score of density in small diameter preform,when crust occurred on the surface of larger diameter preform,additionally,in larger size preform density in surface area was higher and negative density gradient formed from the center to the boundary of the final product.