非晶纳米晶%表面处理%表面氧化%软磁性能
非晶納米晶%錶麵處理%錶麵氧化%軟磁性能
비정납미정%표면처리%표면양화%연자성능
amorphous nanocrystalline%surface treatment%surface oxidation%soft magnetic properties
Fe73.5 Cu1 Nb3 Si13.5 B9纳米晶带材具有优异的软磁性能,在开关电源等领域得到广泛的应用,但Fe73.5 Cu1 Nb3 Si13.5 B9纳米晶带材磁芯在封装过程中存在着环氧树脂严重的不浸润问题,限制了纳米晶带材的应用。通过氧化处理法在带材表面制备了分布均匀、表面光洁、黑棕红色 Fe3 O4和 Fe2 O3氧化膜,氧化膜与带材结合力强,可以作为带材基体与环氧树脂的过渡层,改善了环氧树脂与带材的浸润性。相对于未表面氧化处理的带材,经过表面氧化处理带材的初始磁导率、饱和磁感应强度分别提高了14.6%和4.3%,矫顽力降低了21.6%。
Fe73.5 Cu1 Nb3 Si13.5 B9納米晶帶材具有優異的軟磁性能,在開關電源等領域得到廣汎的應用,但Fe73.5 Cu1 Nb3 Si13.5 B9納米晶帶材磁芯在封裝過程中存在著環氧樹脂嚴重的不浸潤問題,限製瞭納米晶帶材的應用。通過氧化處理法在帶材錶麵製備瞭分佈均勻、錶麵光潔、黑棕紅色 Fe3 O4和 Fe2 O3氧化膜,氧化膜與帶材結閤力彊,可以作為帶材基體與環氧樹脂的過渡層,改善瞭環氧樹脂與帶材的浸潤性。相對于未錶麵氧化處理的帶材,經過錶麵氧化處理帶材的初始磁導率、飽和磁感應彊度分彆提高瞭14.6%和4.3%,矯頑力降低瞭21.6%。
Fe73.5 Cu1 Nb3 Si13.5 B9납미정대재구유우이적연자성능,재개관전원등영역득도엄범적응용,단Fe73.5 Cu1 Nb3 Si13.5 B9납미정대재자심재봉장과정중존재착배양수지엄중적불침윤문제,한제료납미정대재적응용。통과양화처리법재대재표면제비료분포균균、표면광길、흑종홍색 Fe3 O4화 Fe2 O3양화막,양화막여대재결합력강,가이작위대재기체여배양수지적과도층,개선료배양수지여대재적침윤성。상대우미표면양화처리적대재,경과표면양화처리대재적초시자도솔、포화자감응강도분별제고료14.6%화4.3%,교완력강저료21.6%。
Fe73.5 Cu1 Nb3 Si13.5 B9 nanocrystalline strip exhibit excellent soft magnetic properties,and was widely used in the field of switch power supply,etc.But Fe73.5 Cu1 Nb3 Si13.5 B9 nanocrystalline strip magnetic core exis-ted serious infiltration problem of epoxy resin in the process of encapsulation,which limited the application of nanocrystalline strip.We invest the oxidation process on the surface of the strip.The surface of the strip dis-tribute uniformity,smooth,dark red brown oxide film.With strong binding force with the strip,oxide film could be use as a transition layer of strip matrix and epoxy resin,so it could improve the infiltration between the strip and epoxy resin.Compared with the strip without surface oxidation treatment,the initial permeability and saturated magnetic induction intensity of the strip with surface oxidation treatment increased by 14.6% and 4. 3% respectively,and the coercive force was reduced by 2 1 .6%.