刘志明%谢成%吴鹏%刘黎阳
劉誌明%謝成%吳鵬%劉黎暘
류지명%사성%오붕%류려양
间硝基苯磺酸钠%助催化剂%芦苇浆纳米纤维素
間硝基苯磺痠鈉%助催化劑%蘆葦漿納米纖維素
간초기분광산납%조최화제%호위장납미섬유소
sodium m-nitrobenzene sulfonate%cocatalyst%reed pulp nanocrystalline cellulose
以间硝基苯磺酸钠(SMS)为助催化剂,质量分数55%硫酸水解芦苇浆制备纳米纤维素(NCC)。研究反应温度、反应时间以及SMS添加量对NCC的产率及粒径的影响。结果表明NCC最佳制备工艺条件为:反应温度50℃,反应时间3.0h,间硝基苯磺酸钠添加量10%(以芦苇浆质量计)。傅里叶变换红外(FT—IR)光谱分析表明最佳工艺条件制备的NCC为纤维素类物质;透射电子显微镜和扫描电子显微镜图分析表明以SMS为助催化剂制备的的NCC形貌更规整,呈棒状。相同NCC制备工艺条件下,与十二烷基苯磺酸钠(SDBS)和硫酸铜(CuSO。)两种助催化剂相比,助催化剂SMS制备的NCC产率最高。
以間硝基苯磺痠鈉(SMS)為助催化劑,質量分數55%硫痠水解蘆葦漿製備納米纖維素(NCC)。研究反應溫度、反應時間以及SMS添加量對NCC的產率及粒徑的影響。結果錶明NCC最佳製備工藝條件為:反應溫度50℃,反應時間3.0h,間硝基苯磺痠鈉添加量10%(以蘆葦漿質量計)。傅裏葉變換紅外(FT—IR)光譜分析錶明最佳工藝條件製備的NCC為纖維素類物質;透射電子顯微鏡和掃描電子顯微鏡圖分析錶明以SMS為助催化劑製備的的NCC形貌更規整,呈棒狀。相同NCC製備工藝條件下,與十二烷基苯磺痠鈉(SDBS)和硫痠銅(CuSO。)兩種助催化劑相比,助催化劑SMS製備的NCC產率最高。
이간초기분광산납(SMS)위조최화제,질량분수55%류산수해호위장제비납미섬유소(NCC)。연구반응온도、반응시간이급SMS첨가량대NCC적산솔급립경적영향。결과표명NCC최가제비공예조건위:반응온도50℃,반응시간3.0h,간초기분광산납첨가량10%(이호위장질량계)。부리협변환홍외(FT—IR)광보분석표명최가공예조건제비적NCC위섬유소류물질;투사전자현미경화소묘전자현미경도분석표명이SMS위조최화제제비적적NCC형모경규정,정봉상。상동NCC제비공예조건하,여십이완기분광산납(SDBS)화류산동(CuSO。)량충조최화제상비,조최화제SMS제비적NCC산솔최고。
Nanocrystalline cellulose (NCC) was prepared from reed pulp with 55 % (by mass fraction) sulfuric acid and using sodium m-nitrobenzene sulfonate (SMS) as cocatalyst. The effects of reaction temperature and time, the addition of SMS on the yield and the mean size of NCC were studied. The results show that the optimal reaction temperature and time are 50℃ and 3.0 h, respectively, and the additon of sodium m-nitrobenzene sulfonate is 10 % (based on mass of reed pulp). Analysis of fourier transform infrared (FT-IR) spectroscopy show that the prepared NCC with optimal condition is cellulosic substance. Analysis of transmission electron microscopy(TEM) and scanning electron microscopy(SEM) show that the morphology of NCC prepared by adding SMS as cocatalyst appears more regular and rod-like. The yield of NCC with addition of SMS as cocatalyst is the highest under the same preparation technology which is compared with the cocatalyst of sodium dodecyl benzene sulfonate (SDBS) and copper sulfate( CuSO4 ).