齐齐哈尔大学学报(自然科学版)
齊齊哈爾大學學報(自然科學版)
제제합이대학학보(자연과학판)
JOURNAL OF QIQIHAR UNIVERSITY(NATURAL SCIENCE EDITION)
2013年
6期
17-22
,共6页
灰关联分析%物理性能%伴生物%细纱强力
灰關聯分析%物理性能%伴生物%細紗彊力
회관련분석%물이성능%반생물%세사강력
gray relational analysis%physical properties%concomitants%spun yarn strength
对6个批号的打成麻的主要物理指标、伴生物含量以及纺成的细纱强力进行了测试,从打成麻的物理性能和伴生物含量两个方面,分别对细纱的强力进行灰关联分析。分析计算得出打成麻的细度对细纱强力的关联度为0.5706;打成麻的强力对细纱强力的关联度为0.8713;纤维长度对细纱强力的关联度为0.7130;脂蜡质含量对细纱强力的关联度为0.5623;水溶物含量纱强力的关联度为0.6041;木质素含量对细纱强力的关联度为0.5683。从物理性能考虑,发现打成麻的强力对细纱强力影响最大;从伴生物含量考虑,发现果胶含量对细纱强力的影响最大。对细纱强力的关联度为0.5210;果胶含量对细纱强力的关联度为0.7445;半纤维素含量对细纱强力的关联度为0.6041;木质素含量对细纱强力的关联度为0.5683。从物理性能考虑,发现打成麻的强力对细纱强力影响最大;从伴生物含量考虑,发现果胶含量对细纱强力的影响最大。
對6箇批號的打成痳的主要物理指標、伴生物含量以及紡成的細紗彊力進行瞭測試,從打成痳的物理性能和伴生物含量兩箇方麵,分彆對細紗的彊力進行灰關聯分析。分析計算得齣打成痳的細度對細紗彊力的關聯度為0.5706;打成痳的彊力對細紗彊力的關聯度為0.8713;纖維長度對細紗彊力的關聯度為0.7130;脂蠟質含量對細紗彊力的關聯度為0.5623;水溶物含量紗彊力的關聯度為0.6041;木質素含量對細紗彊力的關聯度為0.5683。從物理性能攷慮,髮現打成痳的彊力對細紗彊力影響最大;從伴生物含量攷慮,髮現果膠含量對細紗彊力的影響最大。對細紗彊力的關聯度為0.5210;果膠含量對細紗彊力的關聯度為0.7445;半纖維素含量對細紗彊力的關聯度為0.6041;木質素含量對細紗彊力的關聯度為0.5683。從物理性能攷慮,髮現打成痳的彊力對細紗彊力影響最大;從伴生物含量攷慮,髮現果膠含量對細紗彊力的影響最大。
대6개비호적타성마적주요물리지표、반생물함량이급방성적세사강력진행료측시,종타성마적물이성능화반생물함량량개방면,분별대세사적강력진행회관련분석。분석계산득출타성마적세도대세사강력적관련도위0.5706;타성마적강력대세사강력적관련도위0.8713;섬유장도대세사강력적관련도위0.7130;지사질함량대세사강력적관련도위0.5623;수용물함량사강력적관련도위0.6041;목질소함량대세사강력적관련도위0.5683。종물이성능고필,발현타성마적강력대세사강력영향최대;종반생물함량고필,발현과효함량대세사강력적영향최대。대세사강력적관련도위0.5210;과효함량대세사강력적관련도위0.7445;반섬유소함량대세사강력적관련도위0.6041;목질소함량대세사강력적관련도위0.5683。종물이성능고필,발현타성마적강력대세사강력영향최대;종반생물함량고필,발현과효함량대세사강력적영향최대。
The main physical items, concomitants content of scutched flax from six batches and spun yarn strength were tested. It is studied by the method of grey system analysis in two aspects:physical properties and concomitants content of scutched flax. It calculated that the related degree of scutched flax fineness on spun yarn strength was 0.5706;the related degree of scutched flax strength on spun yarn strength was 0.8713;the related degree of scutched flax fiber length on spun yarn strength was 0.7130;the related degree of fatty wax content on spun yarn strength was 0.5623;the related degree of water-soluble content on spun yarn strength was 0.5210;the related hemi-cellulose content on spun yarn strength was 0.6041;the related degree of lignin content on spun yarn strength was 0.5683. From the physical performance perspective,it found that scutched flax strength has the greatest influence on spun yarn strength;from the concomitants content perspective,it found that pectin content has the greatest influence on spun yarn strength.