信阳师范学院学报（自然科学版）
信暘師範學院學報（自然科學版）
신양사범학원학보（자연과학판）
JOURNAL OF XINYANG NORMAL UNIVERSITY(NATURAL SCIENCE EDITION)
2013年
4期
551-554
,共4页
柔性不饱和聚酯树脂%甲基丙烯酸甲酯%粉煤灰%固化%动力学
柔性不飽和聚酯樹脂%甲基丙烯痠甲酯%粉煤灰%固化%動力學
유성불포화취지수지%갑기병희산갑지%분매회%고화%동역학
flexible unsaturated polyester resin%methyl methacrylate%coal fly ash%cure%kinetics
用差示扫描量热法（ DSC）研究了自制柔性不饱和聚酯/甲基丙烯酸甲酯树脂（ FUP/MMA）和柔性不饱和聚酯/甲基丙烯酸甲酯/T-60改性粉煤灰（ FUP/MMA/CFA）复合体系的固化过程．利用Kissinger法、Oza-wa法求出FUP/MMA和FUP/MMA/CFA两体系固化反应的表观活化能分别为81．578 kJ· mol-1和77．231 kJ · mol-1；用ASTM E698-79标准方法求得两体系固化反应的指前因子lnA分别为20．40 s-1和19．15 s-1；结合Crane方程得到两体系的反应级数n分别为0．9377和0．9359；最终确定了固化反应的动力学方程．用T-β外推法确定了凝胶温度、固化温度和后固化温度等固化工艺温度．
用差示掃描量熱法（ DSC）研究瞭自製柔性不飽和聚酯/甲基丙烯痠甲酯樹脂（ FUP/MMA）和柔性不飽和聚酯/甲基丙烯痠甲酯/T-60改性粉煤灰（ FUP/MMA/CFA）複閤體繫的固化過程．利用Kissinger法、Oza-wa法求齣FUP/MMA和FUP/MMA/CFA兩體繫固化反應的錶觀活化能分彆為81．578 kJ· mol-1和77．231 kJ · mol-1；用ASTM E698-79標準方法求得兩體繫固化反應的指前因子lnA分彆為20．40 s-1和19．15 s-1；結閤Crane方程得到兩體繫的反應級數n分彆為0．9377和0．9359；最終確定瞭固化反應的動力學方程．用T-β外推法確定瞭凝膠溫度、固化溫度和後固化溫度等固化工藝溫度．
용차시소묘량열법（ DSC）연구료자제유성불포화취지/갑기병희산갑지수지（ FUP/MMA）화유성불포화취지/갑기병희산갑지/T-60개성분매회（ FUP/MMA/CFA）복합체계적고화과정．이용Kissinger법、Oza-wa법구출FUP/MMA화FUP/MMA/CFA량체계고화반응적표관활화능분별위81．578 kJ· mol-1화77．231 kJ · mol-1；용ASTM E698-79표준방법구득량체계고화반응적지전인자lnA분별위20．40 s-1화19．15 s-1；결합Crane방정득도량체계적반응급수n분별위0．9377화0．9359；최종학정료고화반응적동역학방정．용T-β외추법학정료응효온도、고화온도화후고화온도등고화공예온도．
The curing kinetics of flexible unsaturated polyester /methyl methacrylate resin ( FUP/MMA) and flexi-ble unsaturated polyester resin/coal fly ash (FUP/MMA/CFA) system was studied with non-isothermal DSC.The ap-parent activation energy (Ea), pre-exponential factor (A) and reaction order (n) were obtained, where Ea =81.578 kJ· mol-1 , lnA =20.40 s-1 and n =0.937 7 for FUP/MMA system and Ea=77.231 kJ· mol -1 , lnA =19.15 s-1 and n =0.935 9 for FUP/MMA/CFA system with Kissinger method, Ozawa method, ASTM E698-79 method and Crane equation .Based on these parameters , kinetic equations for the curing of FUP/MMA and FUP/MMA/CFA sys-tems were established .Gelling temperature , curing temperature and treating temperature for each system were deter-mined by extrapolating T-β.