尝试采用新型柔软平滑剂680对纯棉针织物进行整理,以减少其缝制过程中针洞的产生,提高其内在质量和穿着服用性能。采用正交试验分析获得最佳整理工艺,并与另2种柔软平滑剂的整理效果进行对比。结果表明：柔软平滑剂680在可缝纫性和防针洞性方面效果最显著；最佳整理工艺为：用量2%,温度40℃,时间20 min,浴比1∶10；采用柔软平滑剂整理后,织物的吸水性能、耐磨性能及柔软性能均得到了改善。
상시채용신형유연평활제680대순면침직물진행정리,이감소기봉제과정중침동적산생,제고기내재질량화천착복용성능。채용정교시험분석획득최가정리공예,병여령2충유연평활제적정리효과진행대비。결과표명：유연평활제680재가봉인성화방침동성방면효과최현저；최가정리공예위：용량2%,온도40℃,시간20 min,욕비1∶10；채용유연평활제정리후,직물적흡수성능、내마성능급유연성능균득도료개선。
Novel soften smoothing agent 680 was applied in the cotton knitted fabric finishing in order to reduce the occurrence of holes during practical manufacturing and enhance their quality and wearability. The optimal finishing process was obtained through orthogonal test, and the finishing results were compared with the other two soften smoothing agents. The results showed that the sewability and anti-needle-hole property of fabric finished by novel soften smoothing agent 680 were the best. The optimum finishing technology was:2% of additive dosage, 40 ℃, 20 min and 1∶10 of liquor ratio. The absorbency, wear-resistance and softness of finished fabric were also improved.