合成材料老化与应用
閤成材料老化與應用
합성재료노화여응용
SYNTHETIC MATERIALS AGING AND APPLICATION
2013年
6期
12-13,53
,共3页
麦伟宗%李景%黄李胜%许灯波
麥偉宗%李景%黃李勝%許燈波
맥위종%리경%황리성%허등파
PC/ABS合金%高胶粉%SAN%力学性能
PC/ABS閤金%高膠粉%SAN%力學性能
PC/ABS합금%고효분%SAN%역학성능
PC/ABS alloy%PB%SAN%mechanical property
利用双螺杆挤出机制备PC/ABS合金,探讨了基材不同种类的选择及其比例的调整对PC/ABS合金性能的影响。结果表明:在PC/ABS合金(70/30)体系中,选用23.23%SAN粉料和5.89%高胶粉替代ABS粒料制成的合金缺口冲击强度可达95.04kJ/m2,拉伸强度达58.28MPa,弯曲强度达73.8MPa。
利用雙螺桿擠齣機製備PC/ABS閤金,探討瞭基材不同種類的選擇及其比例的調整對PC/ABS閤金性能的影響。結果錶明:在PC/ABS閤金(70/30)體繫中,選用23.23%SAN粉料和5.89%高膠粉替代ABS粒料製成的閤金缺口遲擊彊度可達95.04kJ/m2,拉伸彊度達58.28MPa,彎麯彊度達73.8MPa。
이용쌍라간제출궤제비PC/ABS합금,탐토료기재불동충류적선택급기비례적조정대PC/ABS합금성능적영향。결과표명:재PC/ABS합금(70/30)체계중,선용23.23%SAN분료화5.89%고효분체대ABS립료제성적합금결구충격강도가체95.04kJ/m2,랍신강도체58.28MPa,만곡강도체73.8MPa。
The PC/ABS alloy was prepared by tw in-screw extruder.The selection of different resin and different resin inverse proportion were discussed.The results show that notch impact strength is 95.04kJ/m2 , the tensile strength is 58.28MPa,the flexural strength is 73.8MPa by adding 23.23% SAN and 5.89% PB into PC/ABS (70/30).