为了提高硼系延期药的质量控制水平，分别研究了原料硼、储存硼及溶剂提纯硼的表面酸碱性、比表面积、X-射线衍射及其颗粒纯度等。结果表明：原料硼储存315 d后酸性杂质增多，XRD曲线中B2 O3衍射峰显著增强，水悬浮液pH值略有降低，颗粒团聚加剧，比表面积由13.4 m2/g减至10.3 m2/g，氧化增重降低约7％。乙醇提纯后的硼粉比表面积增至16.2 m2/g，分散性提高，长期储存的硼粉经溶剂提纯后的XRD曲线中未观察到B2 O3衍射峰，热氧化增重提高约12.0％~18.5％，硼粉纯度得到一定程度的提高。
위료제고붕계연기약적질량공제수평，분별연구료원료붕、저존붕급용제제순붕적표면산감성、비표면적、X-사선연사급기과립순도등。결과표명：원료붕저존315 d후산성잡질증다，XRD곡선중B2 O3연사봉현저증강，수현부액pH치략유강저，과립단취가극，비표면적유13.4 m2/g감지10.3 m2/g，양화증중강저약7％。을순제순후적붕분비표면적증지16.2 m2/g，분산성제고，장기저존적붕분경용제제순후적XRD곡선중미관찰도B2 O3연사봉，열양화증중제고약12.0％~18.5％，붕분순도득도일정정도적제고。
To improve the quality control level of boron type delay composition, the surface acidity, BET specific surface area,X-ray diffraction and the purity of raw boron,stored boron and solvent purified boron were investigated. The results show that,after being stored for 315 days, the amount of acidic impurities in the raw boron increases, the peaks assigned to B2 O3 in the XRD curve increase significantly,the pH value of boron suspension decreases,the agglomeration of boron particles gets worse,the specific surface area reduces from 13. 4 m2/g to 10. 3 m2/g, and the oxidation weight of boron drops by 7%. In contrast, after being purified with ethanol, the specific surface area of boron increases to 16. 2 m2/g, the dispersion of boron is improved, no peaks attributed to B2 O3 is detected, and the thermal oxidation weight of boron increases by 12. 0%-18. 5%. The boron has been purified by the solvents.