通过对 Fe 基非晶合金带材连续施加压力,测试其附近闭合回路电感变化,研究了Fe基非晶合金带材的电感式压磁效应。结果表明,通过测试 Fe基非晶合金带材附近闭合回路电感变化可用来测试和表征Fe基非晶合金带材的压磁性能；在f=1kHz时,Fe基非晶合金带材压磁性能稳定性好,随着压力的增大带材压磁性能升高,在同一压力情况下, Fe73.5 Cu1 Nb3 Si13.5 B9带材压磁性能优于 Fe78 Si9 B13带材；在f=100kHz 时,Fe73.5 Cu1 Nb3 Si13.5 B9带材压磁性能稳定性优于 Fe78 Si9 B13带材,并且 Fe73.5 Cu1 Nb3-Si13.5 B9带材在f=1kHz、压应力为0.69MPa 时具有最佳的压磁性能；在压应力<0.1 MP a 条件下,随着压应力增大,线圈电感值Ls 有一个剧增的上升趋势,铁基非晶带材压磁性能对微小应力更加敏感。
통과대 Fe 기비정합금대재련속시가압력,측시기부근폐합회로전감변화,연구료Fe기비정합금대재적전감식압자효응。결과표명,통과측시 Fe기비정합금대재부근폐합회로전감변화가용래측시화표정Fe기비정합금대재적압자성능；재f=1kHz시,Fe기비정합금대재압자성능은정성호,수착압력적증대대재압자성능승고,재동일압력정황하, Fe73.5 Cu1 Nb3 Si13.5 B9대재압자성능우우 Fe78 Si9 B13대재；재f=100kHz 시,Fe73.5 Cu1 Nb3 Si13.5 B9대재압자성능은정성우우 Fe78 Si9 B13대재,병차 Fe73.5 Cu1 Nb3-Si13.5 B9대재재f=1kHz、압응력위0.69MPa 시구유최가적압자성능；재압응력<0.1 MP a 조건하,수착압응력증대,선권전감치Ls 유일개극증적상승추세,철기비정대재압자성능대미소응력경가민감。
Piezomagnetic effect of Fe-based amorphous alloy ribbon was studied by applying continuous stress to Fe-based amorphous alloy ribbon and testing the nearby closed loop inductance changes.The results show that the piezomagnetic property of Fe-base amorphous alloy ribbon can be characterized by testing the nearby closed loop inductance changes of Fe-base amorphous alloy ribbon.When the frequency was equal to 1kHz,piezomag-netic property of Fe-based amorphous alloy ribbon has a good stability.And piezomagnetic property can be raised by increasing pressure.In the same pressure cases,Fe73.5 Cu1 Nb3 Si13.5 B9 alloy ribbon has a better piezo-magnetic property than that of Fe78 Si9 B13 alloy ribbon.When the frequency was equal to 100kHz,the piezomag-netic property of Fe73.5 Cu1 Nb3 Si13.5 B9 has a better stability than Fe78 Si9 B13 alloy ribbon Fe73.5 Cu1 Nb3 Si13.5 B9 al-loy ribbon show the best piezomagnetic property when the frequency was equal to 1kHz and the compressive stress was equal to 0.69MPa.When the compression stress was less than 0.1 MPa,the inductance of coil has a sharp rising trend with the increase of stress,Fe-based amorphous alloy ribbon was more sensitive to tiny stress.