CAJ | 학술논문

分析半钢子午线轮胎氮气硫化氮气消耗量大的原因，并提出相应解决措施。轮胎氮气硫化过程中氮气消耗量大的主要原因是氮气硫化系统管路（包括硫化机氮气系统管路）存在泄漏问题，尤其是管路连接处、控制阀密封处和密封圈等密封不良，通过采取防止氮气泄漏、增大氮气回收量、减小定型氮气消耗量等措施，有效减小了氮气消耗量。
분석반강자오선륜태담기류화담기소모량대적원인，병제출상응해결조시。륜태담기류화과정중담기소모량대적주요원인시담기류화계통관로（포괄류화궤담기계통관로）존재설루문제，우기시관로련접처、공제벌밀봉처화밀봉권등밀봉불량，통과채취방지담기설루、증대담기회수량、감소정형담기소모량등조시，유효감소료담기소모량。
The root causes of large nitrogen consumption during nitrogen curing process of semi-steel radial tire were analyzed and the corrective actions were proposed. The analysis showed the main root cause was leaking of nitrogen piping system including the tubing within the curing machine. The leaking was even more serious in the joints, valves and seals. To reduce the nitrogen consumption, it was recommended to reduce the leakage of nitrogen in the piping system, increase the amount of nitrogen recycling and reduce the nitrogen consumption in the shaping stage.