采用SRV-IV摩擦磨损实验机(球盘接触方式)考察了凹凸棒石热活化产物作为润滑油添加剂的摩擦学性能;研究了热活化温度对凹凸棒石减摩抗磨性的影响;采用SEM、EDS和XPS分别分析了磨损表面的微观形貌、元素组成及元素化学状态.结果表明,热活化后,凹凸棒石的成分和形貌基本不变;热活化后的凹凸棒石粉体具有更好的减摩抗磨性;热活化的最佳温度为500℃.在添加500℃热活化凹凸棒石的油样润滑下,磨损表面生成 FeOx (FeO、Fe2 O3和FeOOH)和 SiOx 复合陶瓷修复层,从而进一步提高钢-钢摩擦副的摩擦学性能.
採用SRV-IV摩抆磨損實驗機(毬盤接觸方式)攷察瞭凹凸棒石熱活化產物作為潤滑油添加劑的摩抆學性能;研究瞭熱活化溫度對凹凸棒石減摩抗磨性的影響;採用SEM、EDS和XPS分彆分析瞭磨損錶麵的微觀形貌、元素組成及元素化學狀態.結果錶明,熱活化後,凹凸棒石的成分和形貌基本不變;熱活化後的凹凸棒石粉體具有更好的減摩抗磨性;熱活化的最佳溫度為500℃.在添加500℃熱活化凹凸棒石的油樣潤滑下,磨損錶麵生成 FeOx (FeO、Fe2 O3和FeOOH)和 SiOx 複閤陶瓷脩複層,從而進一步提高鋼-鋼摩抆副的摩抆學性能.
채용SRV-IV마찰마손실험궤(구반접촉방식)고찰료요철봉석열활화산물작위윤활유첨가제적마찰학성능;연구료열활화온도대요철봉석감마항마성적영향;채용SEM、EDS화XPS분별분석료마손표면적미관형모、원소조성급원소화학상태.결과표명,열활화후,요철봉석적성분화형모기본불변;열활화후적요철봉석분체구유경호적감마항마성;열활화적최가온도위500℃.재첨가500℃열활화요철봉석적유양윤활하,마손표면생성 FeOx (FeO、Fe2 O3화FeOOH)화 SiOx 복합도자수복층,종이진일보제고강-강마찰부적마찰학성능.
A SRV-IV friction and wear tester (ball-on-disc contact mode)was used to investigate the tribological properties of attapulgite treated by thermal activation as lubricant additive.The effect of thermal temperature on the antifriction and antiwear properties of attapulgite was investigated.The morphology,elemental composition and elementary chemical forms of worn surfaces were analyzed by using SEM,EDS and XPS.The results show that the component and morphology of attapulgite treated thermal activation were unchanged basically.The at-tapulgite powders after thermal activation possess better antifriction and antiwear properties than natural at-tapulgite.The best thermal temperature was 500 ℃.Under the lubrication of oil adding attapulgite treated by 500 ℃.Composite ceramic repairing layer of FeOx (FeO,Fe2 O3 and FeOOH)and SiOx was formed on worn surface.Consequently make further improvement of the tribological property of the steel-steel frictional pair.