利用Deform软件对微型齿轮进行挤压成形模拟分析,优化了模具结构和成形条件,采用组合法设计模数m=0.125 mm、压力角A=20°、齿数z=6、齿顶圆直径d=1 mm微型齿轮热挤压模,采用H62黄铜坯料在650℃的等温条件下正向热挤压,得到质量良好的微型齿轮。
利用Deform軟件對微型齒輪進行擠壓成形模擬分析,優化瞭模具結構和成形條件,採用組閤法設計模數m=0.125 mm、壓力角A=20°、齒數z=6、齒頂圓直徑d=1 mm微型齒輪熱擠壓模,採用H62黃銅坯料在650℃的等溫條件下正嚮熱擠壓,得到質量良好的微型齒輪。
이용Deform연건대미형치륜진행제압성형모의분석,우화료모구결구화성형조건,채용조합법설계모수m=0.125 mm、압력각A=20°、치수z=6、치정원직경d=1 mm미형치륜열제압모,채용H62황동배료재650℃적등온조건하정향열제압,득도질량량호적미형치륜。
Simulation analysis was made on the extrusion forming of a micro-gear by using the Deform software to optimize the key die structure and forming conditions. A hot extru-sion die for the micro-gear with modulus m=0.125 mm, pressure angle A=20° , tooth number z=6 and addendum circle diameter d=1 mm was designed by splitting method in which H62 brass was used as the blank and positive hot extrusion was applied under 650℃ of isother-mal conditions.