电镀与涂饰
電鍍與塗飾
전도여도식
ELECTROPLATING & FINISHING
2014年
6期
225-229
,共5页
王步华%陈姚%于欣伟%秦中海%张莹娇%余子文
王步華%陳姚%于訢偉%秦中海%張瑩嬌%餘子文
왕보화%진요%우흔위%진중해%장형교%여자문
丙烯酸酯聚氨酯%水性乳液%吸水性%耐醇性
丙烯痠酯聚氨酯%水性乳液%吸水性%耐醇性
병희산지취안지%수성유액%흡수성%내순성
acrylate polyurethane%waterborne emulsion%water absorbability%alcohol resistance
以异佛尔酮二异氰酸酯(IPDI)、聚醚二元醇(N210)、甲基丙烯酸甲酯(MMA)等为原料,采用种子乳液聚合法制备了水性丙烯酸酯聚氨酯(PUA)乳液。探讨了异氰酸根指数 R,二羟甲基丙酸(DMPA)、三羟甲基丙烷(TMP)和甲基丙烯酸甲酯(MMA)等用量以及中和度对 PUA 乳液及其漆膜性能的影响,获得了PUA乳液的最佳合成条件:R =1.3,DMPA添加量为PU质量的6%,TMP和MMA的添加量分别为PUA质量的1%和30%,中和度为90%~100%。红外光谱分析表明,成功合成了 PUA 乳液。在优化条件下制备的乳液外观呈蓝色半透明状,平均粒径71.89 nm,黏度为66.13 mPa·s,具有较好的稳定性。以该乳液制备的漆膜附着力1级,硬度H,吸水率13.84%,具有较好的耐醇性。
以異彿爾酮二異氰痠酯(IPDI)、聚醚二元醇(N210)、甲基丙烯痠甲酯(MMA)等為原料,採用種子乳液聚閤法製備瞭水性丙烯痠酯聚氨酯(PUA)乳液。探討瞭異氰痠根指數 R,二羥甲基丙痠(DMPA)、三羥甲基丙烷(TMP)和甲基丙烯痠甲酯(MMA)等用量以及中和度對 PUA 乳液及其漆膜性能的影響,穫得瞭PUA乳液的最佳閤成條件:R =1.3,DMPA添加量為PU質量的6%,TMP和MMA的添加量分彆為PUA質量的1%和30%,中和度為90%~100%。紅外光譜分析錶明,成功閤成瞭 PUA 乳液。在優化條件下製備的乳液外觀呈藍色半透明狀,平均粒徑71.89 nm,黏度為66.13 mPa·s,具有較好的穩定性。以該乳液製備的漆膜附著力1級,硬度H,吸水率13.84%,具有較好的耐醇性。
이이불이동이이청산지(IPDI)、취미이원순(N210)、갑기병희산갑지(MMA)등위원료,채용충자유액취합법제비료수성병희산지취안지(PUA)유액。탐토료이청산근지수 R,이간갑기병산(DMPA)、삼간갑기병완(TMP)화갑기병희산갑지(MMA)등용량이급중화도대 PUA 유액급기칠막성능적영향,획득료PUA유액적최가합성조건:R =1.3,DMPA첨가량위PU질량적6%,TMP화MMA적첨가량분별위PUA질량적1%화30%,중화도위90%~100%。홍외광보분석표명,성공합성료 PUA 유액。재우화조건하제비적유액외관정람색반투명상,평균립경71.89 nm,점도위66.13 mPa·s,구유교호적은정성。이해유액제비적칠막부착력1급,경도H,흡수솔13.84%,구유교호적내순성。
A waterborne acrylate polyurethane (PUA) emulsion was prepared by seed emulsion polymerization from isophorone diisocyanate (IPDI), polyether diol (N210), and methyl methacrylate (MMA), as evidenced by infrared spectroscopic analysis. The influence of isocyanate index R [n (─NCO)/n (─OH)], dosages of dimethylolpropionic acid (DMPA), trimethylolpropane (TMP) and methyl methacrylate (MMA), and neutralization degree on properties of the PUA emulsion and its film was studied. The optimal synthesis conditions of PUA emulsion were obtained as follows: R=1.3, amount of DMPA 6%by mass of PU, dosages of TMP and MMA 1%and 30%by mass of PUA, respectively, and neutralization degree 90%-100%. The emulsion prepared under the optimal conditions is blue and translucent with an average particle size of 71.89 nm and viscosity of 66.13 mPa·s and good stability. The coating prepared from the emulsion has good alcohol resistance, 1-grade adhesion strength,hardness H, and water absorption rate 13.84%.