通过开展中间包控流装置布置的正交试验,研究了反应器结构对钢水流动行为的影响.着重探讨了不同尺寸中间包的控流装置布置规律及其对钢液流动行为和夹杂物去除的影响,定量化得到了双流板坯中间包控流装置布置与死区体积和结构影响因子D的关系.实验结果分析表明:中间包内部分活塞流体积不利于夹杂物去除,死区体积可准确反映钢液的洁净度水平;出水口抽吸作用对钢液流动行为影响较大,挡坝布置在距出水口1000~1300 mm时钢液流动形态较好,夹杂物聚集导致的水口结瘤率低至7.5%;0.0035<D<0.0085时,可获得板坯中间包在普通拉速下的流场特征与挡坝相对位置的关系;中间包内钢液与夹杂物的相对运动速度为大于6×10-5 m·s-1时,夹杂物的上浮速度较大.
通過開展中間包控流裝置佈置的正交試驗,研究瞭反應器結構對鋼水流動行為的影響.著重探討瞭不同呎吋中間包的控流裝置佈置規律及其對鋼液流動行為和夾雜物去除的影響,定量化得到瞭雙流闆坯中間包控流裝置佈置與死區體積和結構影響因子D的關繫.實驗結果分析錶明:中間包內部分活塞流體積不利于夾雜物去除,死區體積可準確反映鋼液的潔淨度水平;齣水口抽吸作用對鋼液流動行為影響較大,擋壩佈置在距齣水口1000~1300 mm時鋼液流動形態較好,夾雜物聚集導緻的水口結瘤率低至7.5%;0.0035<D<0.0085時,可穫得闆坯中間包在普通拉速下的流場特徵與擋壩相對位置的關繫;中間包內鋼液與夾雜物的相對運動速度為大于6×10-5 m·s-1時,夾雜物的上浮速度較大.
통과개전중간포공류장치포치적정교시험,연구료반응기결구대강수류동행위적영향.착중탐토료불동척촌중간포적공류장치포치규률급기대강액류동행위화협잡물거제적영향,정양화득도료쌍류판배중간포공류장치포치여사구체적화결구영향인자D적관계.실험결과분석표명:중간포내부분활새류체적불리우협잡물거제,사구체적가준학반영강액적길정도수평;출수구추흡작용대강액류동행위영향교대,당패포치재거출수구1000~1300 mm시강액류동형태교호,협잡물취집도치적수구결류솔저지7.5%;0.0035<D<0.0085시,가획득판배중간포재보통랍속하적류장특정여당패상대위치적관계;중간포내강액여협잡물적상대운동속도위대우6×10-5 m·s-1시,협잡물적상부속도교대.
Orthogonal experiments of control device arrangement in different slab casting tundishes were carried out to study the influence of the reactor's structure on the flow characteristic of molten steel. The optimal arrangement rule of control devices and its effect on the flow characteristic of molten steel and inclusion removal were mainly analyzed. A quantificational relation of control devices, dead volume and the structure factor D was determined. The results indicate that the steel cleanness can be reflected by dead volume while the piston flow volume is disadvantageous to inclusion removal. There is a great influence of outlet pumping action on the fluid flow pattern, so the best distance between the dam and outlet is 1000 to 1300 mm, which results in the decrease of nozzle blocking rate to 7.5%. The relation between the flow characteristic of molten steel and the dam's relative location is obtained at normal casting speed when 0.0035<D<0.0085. As the relative speed of inclusions to molten steel reaches to 6í10 -5 m·s-1 , the floating speed of inclusions becomes faster.