王俊霖%张友登%刘敏%张萍%欧阳珉路%王志奋
王俊霖%張友登%劉敏%張萍%歐暘珉路%王誌奮
왕준림%장우등%류민%장평%구양민로%왕지강
双层卷焊管%折弯%裂纹
雙層捲銲管%摺彎%裂紋
쌍층권한관%절만%렬문
double layer welding steel pipe%bending%crack
某汽车配件公司生产汽车油管发生折弯开裂现象,采用金相显微镜和扫描电镜等对油管进行观察并分析开裂原因。结果表明:原双层卷焊管表面存在细小裂纹,在折弯过程中,裂纹在外力作用下发生了扩展,最终导致开裂。
某汽車配件公司生產汽車油管髮生摺彎開裂現象,採用金相顯微鏡和掃描電鏡等對油管進行觀察併分析開裂原因。結果錶明:原雙層捲銲管錶麵存在細小裂紋,在摺彎過程中,裂紋在外力作用下髮生瞭擴展,最終導緻開裂。
모기차배건공사생산기차유관발생절만개렬현상,채용금상현미경화소묘전경등대유관진행관찰병분석개렬원인。결과표명:원쌍층권한관표면존재세소렬문,재절만과정중,렬문재외력작용하발생료확전,최종도치개렬。
The bending and fracture of automobile oil pipes occur in a certain automobile mountings company .The causes of fracture were investigated and observed by the metallurgical microscope and scan-ning electron microscope .The results showed that the micro-cracks existed on the surface of double layer welding steel pipe and that the fracture resulted from the crack extension caused by external force in the course of bending .