磷锌硼系(PZB)玻璃%掺铈钇铝石榴石荧光粉(YAG∶Ce)%正交实验%发光性能
燐鋅硼繫(PZB)玻璃%摻鈰釔鋁石榴石熒光粉(YAG∶Ce)%正交實驗%髮光性能
린자붕계(PZB)파리%참시을려석류석형광분(YAG∶Ce)%정교실험%발광성능
P2O5-ZnO-B2O3 (PZB)glass%YAG∶Ce phosphor%orthogonal experiment%luminescent properties
发光玻璃在白光LED照明等技术领域有重要应用,研究发光玻璃可以有效提高 LED器件的发光效率。对复合钇铝石榴石(YAG∶Ce)荧光粉磷锌硼系(PZB)微晶玻璃的发光性能影响因素进行了分析研究。利用荧光光谱等表征手段,通过正交实验方法,讨论了基质玻璃成形方式、荧光粉掺入量和烧结气氛等对微晶玻璃发光性能的影响。研究表明,基质玻璃成形方式和荧光粉掺量对微晶玻璃的发光性能有较大影响:水淬法制备的基质玻璃的发光性能优于浇注法制备的基质玻璃;当荧光粉掺量为20%(质量分数)时,相对发光强度最大,而后又趋于下降;而烧结气氛对发光性能影响不大。采用正交实验法,得出微晶玻璃试样的相对发光强度范围为1081~4577,各因素对发光强度影响顺序为荧光粉掺量>基质玻璃成形方式>烧结温度>烧结气氛。
髮光玻璃在白光LED照明等技術領域有重要應用,研究髮光玻璃可以有效提高 LED器件的髮光效率。對複閤釔鋁石榴石(YAG∶Ce)熒光粉燐鋅硼繫(PZB)微晶玻璃的髮光性能影響因素進行瞭分析研究。利用熒光光譜等錶徵手段,通過正交實驗方法,討論瞭基質玻璃成形方式、熒光粉摻入量和燒結氣氛等對微晶玻璃髮光性能的影響。研究錶明,基質玻璃成形方式和熒光粉摻量對微晶玻璃的髮光性能有較大影響:水淬法製備的基質玻璃的髮光性能優于澆註法製備的基質玻璃;噹熒光粉摻量為20%(質量分數)時,相對髮光彊度最大,而後又趨于下降;而燒結氣氛對髮光性能影響不大。採用正交實驗法,得齣微晶玻璃試樣的相對髮光彊度範圍為1081~4577,各因素對髮光彊度影響順序為熒光粉摻量>基質玻璃成形方式>燒結溫度>燒結氣氛。
발광파리재백광LED조명등기술영역유중요응용,연구발광파리가이유효제고 LED기건적발광효솔。대복합을려석류석(YAG∶Ce)형광분린자붕계(PZB)미정파리적발광성능영향인소진행료분석연구。이용형광광보등표정수단,통과정교실험방법,토론료기질파리성형방식、형광분참입량화소결기분등대미정파리발광성능적영향。연구표명,기질파리성형방식화형광분참량대미정파리적발광성능유교대영향:수쉬법제비적기질파리적발광성능우우요주법제비적기질파리;당형광분참량위20%(질량분수)시,상대발광강도최대,이후우추우하강;이소결기분대발광성능영향불대。채용정교실험법,득출미정파리시양적상대발광강도범위위1081~4577,각인소대발광강도영향순서위형광분참량>기질파리성형방식>소결온도>소결기분。
Luminescent glass was widely used in some high-tech fields such as white LED lighting,which can greatly improve the optical efficiency of LED devices.In this work,some factors influencing the luminescent properties of P2 O5-ZnO-B2 O3 (PZB)glass-ceramics doped with YAG∶Ce phosphor were studied and analysed. Using infrared spectra and orthogonal experimental method,the effects of shaping method,YAG∶Ce phosphor content and sintering atmosphere on the luminescent properties of PZB glass-ceramic were studied.The results shown that,shaping method and phosphor content had great effects on the luminescent properties.When the phosphor content reached up to 20wt%,PZB glass-ceramic has the highest luminous intensity,but when the content continued to rise,the emission intensity decreased.Sintering atmosphere did not make any sense to the luminescent properties.Contrary to sintering atmosphere,shaping method played an important role in the lu-minescent properties.The luminescent properties of matrix glass made by water-quenched method was better than that by pouring method.From the Orthogonal test,it can be seen that the emission intensity of the glass-ceramics ranged from 1 081-4 577 a.u.From high to low,some factors that influenced the emission intensity were YAG∶Ce phosphors content,shaping method,sintering temperature and the sintering atmosphere.