采用紫外辐照法将 N-异丙基丙烯酰胺(NIPAAm)接枝于聚四氟乙烯(PTFE)膜表面,得到聚氮异丙基丙烯酰胺接枝改性 PTFE 膜(PTFE-g-PNIPAAm)。采用SEM和 IR,对接枝前后 PTFE 膜的形貌结构及成分进行表征分析,计算其接枝率和透湿率,并考察其在不同温度下的溶胀性能。结果表明,通过紫外辐照,PNIPAAm 接枝于 PTFE 膜表面；当NIPAAm单体浓度为5%(质量分数)时,接枝率最高；PTFE 膜的透湿率在接枝后显著降低；PTFE-g-PNIPAAm膜的溶胀行为在32℃附近发生明显变化。该接枝改性多孔膜有望用作具有温敏特性的易剥离皮肤伤口敷料。
채용자외복조법장 N-이병기병희선알(NIPAAm)접지우취사불을희(PTFE)막표면,득도취담이병기병희선알접지개성 PTFE 막(PTFE-g-PNIPAAm)。채용SEM화 IR,대접지전후 PTFE 막적형모결구급성분진행표정분석,계산기접지솔화투습솔,병고찰기재불동온도하적용창성능。결과표명,통과자외복조,PNIPAAm 접지우 PTFE 막표면；당NIPAAm단체농도위5%(질량분수)시,접지솔최고；PTFE 막적투습솔재접지후현저강저；PTFE-g-PNIPAAm막적용창행위재32℃부근발생명현변화。해접지개성다공막유망용작구유온민특성적역박리피부상구부료。
N-isopropyl acrylamide (NIPAAm)grafted polytetrafluorothylene (PTFE)was prepared by UV irra-diation.The grafted PTFE membrane was observed by SEM and its compositions was analyzed by IR.In addi-tion,the grafting ratio and the water vapor transmission rate were calculated,and the swelling behaviors in dif-ferent temperatures were studied.The results show that,NIPAAm has been grafted onto PTFE membrane successfully and the grafting ratio was up to the maximum when the concentration of NIPAAm monomer was 5wt%;the water vapor transmission rate has dropped obviously;also,the swelling behavior of PTFE-g-PNIPAAm membrane has changed dramatically at near 32 ℃,which was the lower critical solution temperature (LCST)of PNIPAAm hydrogel.So,the PTFE-g-PNIPAAm membrane has the potential to be used as the wound dressing with easily-stripped property.