大型铸锻件
大型鑄鍛件
대형주단건
HEAVY CASTING AND FORGING
2014年
4期
11-12
,共2页
ASTM A668 CL.E钢%回火温度%力学性能
ASTM A668 CL.E鋼%迴火溫度%力學性能
ASTM A668 CL.E강%회화온도%역학성능
ASTM A668 CL.E steel%tempering temperature%mechanical property
通过研究奥氏体化温度、冷却方式、回火温度对ASTM A668 CL．E钢强度、塑性及韧性的影响，确定最合理的热处理工艺为870℃奥氏体化后加速冷却＋670℃回火。
通過研究奧氏體化溫度、冷卻方式、迴火溫度對ASTM A668 CL．E鋼彊度、塑性及韌性的影響，確定最閤理的熱處理工藝為870℃奧氏體化後加速冷卻＋670℃迴火。
통과연구오씨체화온도、냉각방식、회화온도대ASTM A668 CL．E강강도、소성급인성적영향，학정최합리적열처리공예위870℃오씨체화후가속냉각＋670℃회화。
By researching on the influence of austenitizing temperature , cooling method and tempering temperature on the strength, plasticity and ductility of ASTM A668 CL.E steel, it is confirmed that the most reasonable heat treat-ment process is accelerated cooling after austenitizing at 870℃+tempering at 670℃.