胶粒晶体%晶体生长%自组装%聚苯乙烯%微球%垂直沉积
膠粒晶體%晶體生長%自組裝%聚苯乙烯%微毬%垂直沉積
효립정체%정체생장%자조장%취분을희%미구%수직침적
colloidal crystals%crystal growth%self assembly%polystyrene%microspheres%vertical deposition
采用垂直沉积法组装了二元聚苯乙烯胶粒晶体,研究了两种聚苯乙烯胶体微球的粒径比、质量比、温度和分散介质中乙二醇含量等因素对二元聚苯乙烯胶粒晶体组装花样的影响.粒径比>4.45、质量比≥74:26是形成面心立方二元聚苯乙烯胶粒晶体的必要条件.组装温度为60℃,分散介质中乙二醇质量分数为6%时,可得到更高质量的二元聚苯乙烯胶体晶体.胶体微球二元垂直沉积机理研究表明:两种聚苯乙烯胶体微球是同时在基片的表面进行组装的;胶体微球在介质中的布朗运动、沉降速率及其在基片表面的组装速率三者之间匹配越好,所得二元聚苯乙烯胶粒晶体质量越高.
採用垂直沉積法組裝瞭二元聚苯乙烯膠粒晶體,研究瞭兩種聚苯乙烯膠體微毬的粒徑比、質量比、溫度和分散介質中乙二醇含量等因素對二元聚苯乙烯膠粒晶體組裝花樣的影響.粒徑比>4.45、質量比≥74:26是形成麵心立方二元聚苯乙烯膠粒晶體的必要條件.組裝溫度為60℃,分散介質中乙二醇質量分數為6%時,可得到更高質量的二元聚苯乙烯膠體晶體.膠體微毬二元垂直沉積機理研究錶明:兩種聚苯乙烯膠體微毬是同時在基片的錶麵進行組裝的;膠體微毬在介質中的佈朗運動、沉降速率及其在基片錶麵的組裝速率三者之間匹配越好,所得二元聚苯乙烯膠粒晶體質量越高.
채용수직침적법조장료이원취분을희효립정체,연구료량충취분을희효체미구적립경비、질량비、온도화분산개질중을이순함량등인소대이원취분을희효립정체조장화양적영향.립경비>4.45、질량비≥74:26시형성면심립방이원취분을희효립정체적필요조건.조장온도위60℃,분산개질중을이순질량분수위6%시,가득도경고질량적이원취분을희효체정체.효체미구이원수직침적궤리연구표명:량충취분을희효체미구시동시재기편적표면진행조장적;효체미구재개질중적포랑운동、침강속솔급기재기편표면적조장속솔삼자지간필배월호,소득이원취분을희효립정체질량월고.
Binary colloidal crystals were fabricated by a vertical deposition method with two sub-micrometer size polystyrene ( PS) microspheres. The self-assembled patterns of binary colloidal crystals ( bCCs) were investigated by varying the size ratio, the mass ratio of PS microspheres, the temperature and content of ethylene glycol in water. It is found that PS binary colloidal crystals with face-cen-tered cube (fcc) arrangement can be obtained while the size ratio is more than 4. 45 and the mass ratio is not less that 74:26. High-quality PS binary colloidal crystals are easily generated at the temperature of 60℃ and the mass fraction of ethylene glycol in dispersing medium of 6%. The study also shows that self-assembly of two PS microspheres on the substrate surface is operated at the same time, and in this regard the vertical deposition method has a great deal of difference from other methods. In addition, PS binary colloidal crystals have a higher quality with the increase of matching between Brownian motion, sedimentation rate of PS colloidal microspheres in water, and self-assembly rate on the substrate surface.