A new diamond grinding wheel was prepared by powder injection molding and vacuum brazing,the new diamond wheel had a larger number of cutting edges which were artificially ordered so as to have big chip storage space,and it realized strong adhesion between diamonds and brazing al-loy due to vacuum brazing.The paper discussed the grinding performance of the new diamond wheel in machining Al2 O 3 ceramic.The experimental results indicate that the quality of the machined work-piece surface is better than that machined by the conventional resin bond diamond wheel,the surface roughness is as 0.68 μm when the feed speed is as 40 mm/sec and the depth of grinding is as 40 μm, and the forces decreases by 12%~17% in compassion with conventional resin bond diamond wheel, and grinding temperature is reduced 80~120℃.