以甲基丙烯酸为原料，N ，N’亚甲基双丙烯酰胺为交联剂，过硫酸钾为引发剂，自由基引发聚合制备聚甲基丙烯酸水凝胶，研究了聚甲基丙烯酸水凝胶的溶胀率、保水率，讨论了交联剂、引发剂的用量以及pH、盐溶液浓度对溶胀性能的影响．实验结果表明：当合成温度为70℃时，p H＝8，盐溶液浓度为0，交联剂、引发剂用量分别为反应物质量的0.6％，1.0％，制备出来的水凝胶的溶胀性能最好．
이갑기병희산위원료，N ，N’아갑기쌍병희선알위교련제，과류산갑위인발제，자유기인발취합제비취갑기병희산수응효，연구료취갑기병희산수응효적용창솔、보수솔，토론료교련제、인발제적용량이급pH、염용액농도대용창성능적영향．실험결과표명：당합성온도위70℃시，p H＝8，염용액농도위0，교련제、인발제용량분별위반응물질량적0.6％，1.0％，제비출래적수응효적용창성능최호．
Using methacrylic acid as raw material ,N ,N' methylene bisacrylamide as crosslinker ,potassium persulfate as an initiator ,the poly methyl methacrylate hydrogel was composed by the reaction of radical polymerization .The swelling ratio and water retention of poly methyl methacrylate hydrogel was researched ,even ,not only the amount of crosslinking and ini-tiator but also the performance impact by the factors of pH and salt concentration was discussed .The experimental results showed that the swelling properties of the preparative hydrogel was best in the condition of the sintering temperature was 70℃ ,pH=8 ,the concentration of the salt was 0 ,the amount of crosslinker and initiator was 0.6% ,1.0% of reactants .