实用口腔医学杂志
實用口腔醫學雜誌
실용구강의학잡지
JOURNAL OF PRACTICAL STOMATOLOGY
2014年
5期
641-644
,共4页
李玉梅%赵铱民%查年保%马威
李玉梅%趙銥民%查年保%馬威
리옥매%조의민%사년보%마위
钛%微弧氧化%成骨细胞%基因表达
鈦%微弧氧化%成骨細胞%基因錶達
태%미호양화%성골세포%기인표체
Titanium%Micro-arc oxidation%Osteoblast%Gene expression
目的:研究微弧氧化纯钛表面对MC3 T3-E 1细胞胶原分泌和成骨相关基因表达的影响。方法:纯钛圆片分为2个组:微弧氧化组(MAO)和抛光组(PT),培养板表面(TC)作为对照组。用场发射扫描电镜(FESEM)观察试样表面形态,表面粗糙度仪测量其表面粗糙度。将细胞接种于3组材料表面体外培养,培养第12天用粘胶纤维红染色检测细胞胶原分泌,第16天RT-PCR检测细胞成骨相关基因表达。结果:纯钛表面经微弧氧化处理后形成一层多孔氧化层,表面粗糙度增加(P<0.01)。细胞在MAO组试件表面的胶原分泌高于PT或TC组表面(P<0.05)。细胞在MAO组试件表面OSX、COL-Iα1及OPN基因的表达均稍高于PT表面。结论:相比于纯钛抛光表面,微弧氧化纯钛表面更能促进MC3 T3-E 1细胞胶原分泌。
目的:研究微弧氧化純鈦錶麵對MC3 T3-E 1細胞膠原分泌和成骨相關基因錶達的影響。方法:純鈦圓片分為2箇組:微弧氧化組(MAO)和拋光組(PT),培養闆錶麵(TC)作為對照組。用場髮射掃描電鏡(FESEM)觀察試樣錶麵形態,錶麵粗糙度儀測量其錶麵粗糙度。將細胞接種于3組材料錶麵體外培養,培養第12天用粘膠纖維紅染色檢測細胞膠原分泌,第16天RT-PCR檢測細胞成骨相關基因錶達。結果:純鈦錶麵經微弧氧化處理後形成一層多孔氧化層,錶麵粗糙度增加(P<0.01)。細胞在MAO組試件錶麵的膠原分泌高于PT或TC組錶麵(P<0.05)。細胞在MAO組試件錶麵OSX、COL-Iα1及OPN基因的錶達均稍高于PT錶麵。結論:相比于純鈦拋光錶麵,微弧氧化純鈦錶麵更能促進MC3 T3-E 1細胞膠原分泌。
목적:연구미호양화순태표면대MC3 T3-E 1세포효원분비화성골상관기인표체적영향。방법:순태원편분위2개조:미호양화조(MAO)화포광조(PT),배양판표면(TC)작위대조조。용장발사소묘전경(FESEM)관찰시양표면형태,표면조조도의측량기표면조조도。장세포접충우3조재료표면체외배양,배양제12천용점효섬유홍염색검측세포효원분비,제16천RT-PCR검측세포성골상관기인표체。결과:순태표면경미호양화처리후형성일층다공양화층,표면조조도증가(P<0.01)。세포재MAO조시건표면적효원분비고우PT혹TC조표면(P<0.05)。세포재MAO조시건표면OSX、COL-Iα1급OPN기인적표체균초고우PT표면。결론:상비우순태포광표면,미호양화순태표면경능촉진MC3 T3-E 1세포효원분비。
Objective:To investigate the effects of titanium surface modified by micro-arc oxidation (MAO)on the collagen secre-tion and the expression of osteogenesis-related genes of MC3T3-E1 cells.Methods:Pure titanium discs were divided into two groups:Titanium with modified surface by MAO(MAO group)and titanium with polished surface(PT group).Tissue culture polysty-rene plates (TC)were used as controls.Surface morphology of the samples was examined by field-emission scanning electron micros-copy(FESEM).Surface roughness of samples was measured by surface roughness meter.MC3T3-E1 cells were cultured on the sur-face of the samples and the collagen secretion on the samples was measured by sirius red-based colorimetric microassay after 12 days of culture.On day 16 of culture,the expression of osteogenesis-related genes was examined by RT-PCR.Results:A porous oxide layer was observed on the surface of MAO treated samples and the surface roughness was more than that of PT group(P<0.01 ). Cells in MAO group showed higher collagen secretion than in PT or TC groups(P<0.05).MAO treated surface induced higher OSX, COL-Iα1 and OPN expression than PT.Conclusion:MAO treated titanium surface may induce more collagen secretion of MC3T3-E1 cells than PT.