试验研究了单机架双卷取四辊可逆热轧机生产5182铝合金时，产生“中凸度超标+中间波浪”缺陷的原因。结果表明：工作辊原始凸度太小、道次压下量不合理、乳液喷淋压力太小是导致产生该缺陷的主要原因。通过增大工作辊原始凸度、优化道次压下量、提高乳液喷淋压力可以消除此缺陷。
시험연구료단궤가쌍권취사곤가역열알궤생산5182려합금시，산생“중철도초표+중간파랑”결함적원인。결과표명：공작곤원시철도태소、도차압하량불합리、유액분림압력태소시도치산생해결함적주요원인。통과증대공작곤원시철도、우화도차압하량、제고유액분림압력가이소제차결함。
"The middle of the crown superscalar + wave" of the defect resulted from 5182 aluminum alloy produced by single twin winding four-high reversing hot rolling mill was researched experimentally, the results show that the defects are caused because the original work roll crown is too small and pass reduction is unreasonable, emulsion spraying pressure is too small. The defects can be deleted by increasing the original work roll crown, optimization pass reduction, improving emulsion spray pressure .