当代化工
噹代化工
당대화공
CONTEMPORARY CHEMICAL INDUSTRY
2014年
11期
2249-2252
,共4页
硼酸酯%酯化%合成
硼痠酯%酯化%閤成
붕산지%지화%합성
Borate ester%Coupling agent%Synthesis
以硼酸、异丙醇和十八醇为主要原料,催化剂是采用DNW-1强酸性离子交换树脂,在氮气保护下合成了硼酸酯偶联剂。考察了带水剂及物料摩尔比对酯化率的影响,并用红外光谱和1H NMR对硼酸酯进行了表征。研究发现:在n(硼酸)∶n(十八醇)∶n(异丙醇)=0.9∶2.0∶1.2的条件下,并采用苯和甲苯混合带水剂时,酯化率可达到94.57%。利用所合成的硼酸酯偶联剂应用于水镁石/HDPE 复合体系中,结果表明:改性水镁石/HDPE体系的拉伸强度高于未改性水镁石/HDPE体系的拉伸强度。添加量为50%时,改性水镁石的拉伸性能比未改性前提高了3.1%,LOI值为24.5。
以硼痠、異丙醇和十八醇為主要原料,催化劑是採用DNW-1彊痠性離子交換樹脂,在氮氣保護下閤成瞭硼痠酯偶聯劑。攷察瞭帶水劑及物料摩爾比對酯化率的影響,併用紅外光譜和1H NMR對硼痠酯進行瞭錶徵。研究髮現:在n(硼痠)∶n(十八醇)∶n(異丙醇)=0.9∶2.0∶1.2的條件下,併採用苯和甲苯混閤帶水劑時,酯化率可達到94.57%。利用所閤成的硼痠酯偶聯劑應用于水鎂石/HDPE 複閤體繫中,結果錶明:改性水鎂石/HDPE體繫的拉伸彊度高于未改性水鎂石/HDPE體繫的拉伸彊度。添加量為50%時,改性水鎂石的拉伸性能比未改性前提高瞭3.1%,LOI值為24.5。
이붕산、이병순화십팔순위주요원료,최화제시채용DNW-1강산성리자교환수지,재담기보호하합성료붕산지우련제。고찰료대수제급물료마이비대지화솔적영향,병용홍외광보화1H NMR대붕산지진행료표정。연구발현:재n(붕산)∶n(십팔순)∶n(이병순)=0.9∶2.0∶1.2적조건하,병채용분화갑분혼합대수제시,지화솔가체도94.57%。이용소합성적붕산지우련제응용우수미석/HDPE 복합체계중,결과표명:개성수미석/HDPE체계적랍신강도고우미개성수미석/HDPE체계적랍신강도。첨가량위50%시,개성수미석적랍신성능비미개성전제고료3.1%,LOI치위24.5。
Using boric acid, isopropanol and octadecanol as main raw materials, strong acid ion exchange resin DNW-1 as catalyst, the borate ester coupling agent was prepared in N2 atmosphere condition. The influence of water carrying agent and mole ratio of raw materials on esterification rate was studied, and the borate ester coupling agent was characterized by IR and1H NMR. The results show that the best reaction conditions of the esterification reaction are as follows: the best water carrying agent is the mixture of benzol and toluene,n(boric acid):n(octadecanol):n(isopropanol)= 0.9: 2.0: 1.2; under above conditions, the esterification rate can reach to 94.57%.And the borate ester coupling agent prepared was used in the composite of brucite/HDPE. The result shows that the tensile strength of modified brucite/HDPE is better than the unmodified brucite/HDPE; when dosage of the borate ester coupling agent is 50%, the tensile strength of modified brucite/HDPE can increase by about 3.1%, and the value of LOI is 24.5.