磁性氧化石墨烯%固定化酶%果胶酶%酶催化动力学%回收利用
磁性氧化石墨烯%固定化酶%果膠酶%酶催化動力學%迴收利用
자성양화석묵희%고정화매%과효매%매최화동역학%회수이용
magnetic graphene oxide%immobilisation of enzyme%pectinase%kinetic parameters of enzymatic catalysis%recover and reuse
磁性氧化石墨烯固定化酶的研究鲜见报道,本实验采用水热沉淀法制备了铁磁性氧化石墨烯(magnetic graphene oxide,MGO),通过交联剂固定化果胶酶。采用红外光谱和SEM表征了制备的MGO的活性基团和特性。结果表明MGO具有—OH等亲水活性基团,可以较好地分散在水相催化体系中。磁性氧化石墨烯的蛋白上载量可达1453mg/g MGO,远高于颗粒活性碳,硅藻土和粉末活性炭的上载量。并且研究了酶催化的动力学,酶的催化转化值7.41h?1,催化效率0.98mL/(h?mg),Km7.55mg/mL。固定化酶稳定性明显增强,且重复使用10次活性仍然可以保持在初始酶活的58%。
磁性氧化石墨烯固定化酶的研究鮮見報道,本實驗採用水熱沉澱法製備瞭鐵磁性氧化石墨烯(magnetic graphene oxide,MGO),通過交聯劑固定化果膠酶。採用紅外光譜和SEM錶徵瞭製備的MGO的活性基糰和特性。結果錶明MGO具有—OH等親水活性基糰,可以較好地分散在水相催化體繫中。磁性氧化石墨烯的蛋白上載量可達1453mg/g MGO,遠高于顆粒活性碳,硅藻土和粉末活性炭的上載量。併且研究瞭酶催化的動力學,酶的催化轉化值7.41h?1,催化效率0.98mL/(h?mg),Km7.55mg/mL。固定化酶穩定性明顯增彊,且重複使用10次活性仍然可以保持在初始酶活的58%。
자성양화석묵희고정화매적연구선견보도,본실험채용수열침정법제비료철자성양화석묵희(magnetic graphene oxide,MGO),통과교련제고정화과효매。채용홍외광보화SEM표정료제비적MGO적활성기단화특성。결과표명MGO구유—OH등친수활성기단,가이교호지분산재수상최화체계중。자성양화석묵희적단백상재량가체1453mg/g MGO,원고우과립활성탄,규조토화분말활성탄적상재량。병차연구료매최화적동역학,매적최화전화치7.41h?1,최화효솔0.98mL/(h?mg),Km7.55mg/mL。고정화매은정성명현증강,차중복사용10차활성잉연가이보지재초시매활적58%。
Ferric magnetic graphene oxide was prepared using hydrothermal precipitation method,and immobilized pectinase on it with crosslinking regeant. There is few report on the immobilisation of pectinase on magnetic graphene oxide (MGO). Active groups and characteristics were characterized using FT-IR and SEM analysis. It was illustrated that active groups (—OH etc.) were formed on MGO,which lead to well dispersion in water phase. High loading densities (1453mg per g of support) was obtained,which is higher than that of activated carbon and diatomite. In addition,kinetic parameters of enzymatic catalysis were investigated,and characterized by Kcat 7.41h?1,catalytic efficiency (Kcat/Km) 0.98mL/(h·mg) and Km 7.55mg/mL. Stability of immobilized enzyme was enhanced and 58%residual activity was maintained after 10 cycle of application.