PBS%wood flour%processing technology%rheologicai property
采用高级毛细管流变仪,分别测定PBS及PBS/杨木粉全降解木塑复合材料的流变性能,研究了不同挤出温度、不同木粉含量对复合材料加工性能的影响。以流变性能测试为参考,改变加工工艺,采用熔融共混法制备了PBS/杨木粉全降解木塑复合材料,并测试其性能。结果表明,随着木粉用量的增加,体系流动性明显下降,可加工的温度范围越来越窄,大致木粉填充量每提高5%,需要升高5℃才能保证粘度变化不大;不同加工工艺对所制备的PBS/杨木粉木塑复合材料性能有较大影响;综合流变性能和力学性能,木粉含量为30%、35%、40%、45%和50%的PBS/杨木粉全降解木塑复合材料的较佳加工温度分别为120、125、125、130和135℃。
採用高級毛細管流變儀,分彆測定PBS及PBS/楊木粉全降解木塑複閤材料的流變性能,研究瞭不同擠齣溫度、不同木粉含量對複閤材料加工性能的影響。以流變性能測試為參攷,改變加工工藝,採用鎔融共混法製備瞭PBS/楊木粉全降解木塑複閤材料,併測試其性能。結果錶明,隨著木粉用量的增加,體繫流動性明顯下降,可加工的溫度範圍越來越窄,大緻木粉填充量每提高5%,需要升高5℃纔能保證粘度變化不大;不同加工工藝對所製備的PBS/楊木粉木塑複閤材料性能有較大影響;綜閤流變性能和力學性能,木粉含量為30%、35%、40%、45%和50%的PBS/楊木粉全降解木塑複閤材料的較佳加工溫度分彆為120、125、125、130和135℃。
채용고급모세관류변의,분별측정PBS급PBS/양목분전강해목소복합재료적류변성능,연구료불동제출온도、불동목분함량대복합재료가공성능적영향。이류변성능측시위삼고,개변가공공예,채용용융공혼법제비료PBS/양목분전강해목소복합재료,병측시기성능。결과표명,수착목분용량적증가,체계류동성명현하강,가가공적온도범위월래월착,대치목분전충량매제고5%,수요승고5℃재능보증점도변화불대;불동가공공예대소제비적PBS/양목분목소복합재료성능유교대영향;종합류변성능화역학성능,목분함량위30%、35%、40%、45%화50%적PBS/양목분전강해목소복합재료적교가가공온도분별위120、125、125、130화135℃。
The influence of different temperature and contents of poplar wood flour(WF) on the rheological behavior of the composites were researched through measuring the rheological behavior of the poly(butylene succinate)(PBS) and the PBS/WF composites by advanced capillary rheometer.Using rheological properties of composites as a reference,changing processing technology,PBS/WF composites were prepared by melt blending and injection molding,after that,we tested the performance of the samples.The results showed that,with increasing of the amounts of WF,the melt flow properties of the composite had a great decline and the processing temperature range became more and more narrow;different processing technologies had a certain impact on the performance of PBS/WF composites.Take mechanical and rheological properties into consideration,the optimum processing temperature of the PBS/poplar wood flour composites were 120,125,125,130 and 135℃ with 30%,35%,40%,45% and 50% of poplar wood flour,respectively.