功能材料
功能材料
공능재료
JOURNAL OF FUNCTIONAL MATERIALS
2012年
23期
3240-3244
,共5页
付春娟%胡竞之%刘建华%李松梅%于美%游盾
付春娟%鬍競之%劉建華%李鬆梅%于美%遊盾
부춘연%호경지%류건화%리송매%우미%유순
还原剂%化学镀%HGM%Ni-P%核%壳粒子%微波吸收性能
還原劑%化學鍍%HGM%Ni-P%覈%殼粒子%微波吸收性能
환원제%화학도%HGM%Ni-P%핵%각입자%미파흡수성능
reducing agent%electroless plating%HGM/Ni-P%core-shell particles%microwave absorption properties
以NaH2PO2为还原剂,采用化学镀方法,在空心玻璃微球表面沉积Ni-P层,获得了轻质空心玻璃微球/Ni-P核/壳复合粒子(简称为HGM/Ni-P核/壳粒子)。采用扫描电子显微镜(SEM)、能谱仪(EDX)、X射线衍射仪(XRD)以及网络矢量分析仪(VNA)研究了化学镀过程中不同还原剂用量对复合粒子形貌、结构、成分及其微波吸收性能的影响规律。结果表明,随着还原剂NaH2PO2用量的增大,HGM/Ni-P核/壳粒子的表面形貌变化不大,壳层中P含量随之升高,非晶成分增多。HGM在镀覆后介电性质与磁导率较镀覆前显著提高。随着NaH2PO2由20g/L增加到30g/L时ε′和ε″的响应峰向高频移动,增加到40g/L时其响应峰消失,且介电常数下降。同时,HGM/Ni-P核/壳粒子的μ′和μ″曲线中6~8GHz处代表自然共振的峰随着NaH2PO2浓度的增加而消失。
以NaH2PO2為還原劑,採用化學鍍方法,在空心玻璃微毬錶麵沉積Ni-P層,穫得瞭輕質空心玻璃微毬/Ni-P覈/殼複閤粒子(簡稱為HGM/Ni-P覈/殼粒子)。採用掃描電子顯微鏡(SEM)、能譜儀(EDX)、X射線衍射儀(XRD)以及網絡矢量分析儀(VNA)研究瞭化學鍍過程中不同還原劑用量對複閤粒子形貌、結構、成分及其微波吸收性能的影響規律。結果錶明,隨著還原劑NaH2PO2用量的增大,HGM/Ni-P覈/殼粒子的錶麵形貌變化不大,殼層中P含量隨之升高,非晶成分增多。HGM在鍍覆後介電性質與磁導率較鍍覆前顯著提高。隨著NaH2PO2由20g/L增加到30g/L時ε′和ε″的響應峰嚮高頻移動,增加到40g/L時其響應峰消失,且介電常數下降。同時,HGM/Ni-P覈/殼粒子的μ′和μ″麯線中6~8GHz處代錶自然共振的峰隨著NaH2PO2濃度的增加而消失。
이NaH2PO2위환원제,채용화학도방법,재공심파리미구표면침적Ni-P층,획득료경질공심파리미구/Ni-P핵/각복합입자(간칭위HGM/Ni-P핵/각입자)。채용소묘전자현미경(SEM)、능보의(EDX)、X사선연사의(XRD)이급망락시량분석의(VNA)연구료화학도과정중불동환원제용량대복합입자형모、결구、성분급기미파흡수성능적영향규률。결과표명,수착환원제NaH2PO2용량적증대,HGM/Ni-P핵/각입자적표면형모변화불대,각층중P함량수지승고,비정성분증다。HGM재도복후개전성질여자도솔교도복전현저제고。수착NaH2PO2유20g/L증가도30g/L시ε′화ε″적향응봉향고빈이동,증가도40g/L시기향응봉소실,차개전상수하강。동시,HGM/Ni-P핵/각입자적μ′화μ″곡선중6~8GHz처대표자연공진적봉수착NaH2PO2농도적증가이소실。
Based on the NaH2PO2 as reducing agent,Ni-P layer was deposited on the surface of microspheres by electroless plating,getting the lightweight hollow glass microspheres/Ni-P core/shell particles(referred to as HGM/Ni-P core/shell particles).The phase structures,morphologies,particle size,shell thickness,chemical compositions and the microwave absorbing properties of the core-shell particles have been characterized by X-ray diffraction(XRD),scanning electron microscope(SEM),energy dispersive X-ray spectroscopy(EDS) and vector network analyzer(VNA),respectively.The results showed that with the increaseing of the reducing agent,surface morphology of HGM/Ni-P core/shell particles shows few different,but P content of shell layer increases,and amorphous structure in the shell change,amorphous ingredients increase.The dielectric properties and magnetic permeability of HGM after plating was greatly improved.As the concentration of NaH2PO2 increased from 20 to 30g/L,the resonance peak of ε′ and ε″ moved to higher frequency,as the concentration of NaH2PO2 got to 40g/L,the resonance peak disappeared and the dielectric constant reduced.Meanwhile,the fluctuation of μ′ and μ″ at 6-8GHz disappeared as the NaH2PO2 increased.