刘以凡%刘明华%田晨%郑梦慧
劉以凡%劉明華%田晨%鄭夢慧
류이범%류명화%전신%정몽혜
包埋%荆树皮栲胶%球形纤维素吸附剂%盐酸小檗碱
包埋%荊樹皮栲膠%毬形纖維素吸附劑%鹽痠小檗堿
포매%형수피고효%구형섬유소흡부제%염산소벽감
embed%black wattle extract%spherical cellulose adsorbent%berberine hydrochloride
以马尾松硫酸盐浆纸浆纤维素为原料,利用热溶胶转相法,在纤维素再生过程中将荆树皮栲胶包埋在纤维素基体上,制备出包埋型球形纤维素吸附剂ESCA,并考察其对盐酸小檗碱的吸附效果。结果表明,当荆树皮栲胶用量为1.00%,碳酸钙用量为6.67%,明胶用量为3.33%,油酸钠用量为0.50%时,制得的吸附剂ESCA的含水率为73.2%,比表面积为436.2m2/g,荆树皮栲胶的包埋率为98.26%。当盐酸小檗碱初始质量浓度为200mg/L,溶液pH值为7,吸附时间为3.0h,吸附温度为30℃时,ESCA对盐酸小檗碱的吸附率为95.28%,平衡吸附容量为23.82mg/g。
以馬尾鬆硫痠鹽漿紙漿纖維素為原料,利用熱溶膠轉相法,在纖維素再生過程中將荊樹皮栲膠包埋在纖維素基體上,製備齣包埋型毬形纖維素吸附劑ESCA,併攷察其對鹽痠小檗堿的吸附效果。結果錶明,噹荊樹皮栲膠用量為1.00%,碳痠鈣用量為6.67%,明膠用量為3.33%,油痠鈉用量為0.50%時,製得的吸附劑ESCA的含水率為73.2%,比錶麵積為436.2m2/g,荊樹皮栲膠的包埋率為98.26%。噹鹽痠小檗堿初始質量濃度為200mg/L,溶液pH值為7,吸附時間為3.0h,吸附溫度為30℃時,ESCA對鹽痠小檗堿的吸附率為95.28%,平衡吸附容量為23.82mg/g。
이마미송류산염장지장섬유소위원료,이용열용효전상법,재섬유소재생과정중장형수피고효포매재섬유소기체상,제비출포매형구형섬유소흡부제ESCA,병고찰기대염산소벽감적흡부효과。결과표명,당형수피고효용량위1.00%,탄산개용량위6.67%,명효용량위3.33%,유산납용량위0.50%시,제득적흡부제ESCA적함수솔위73.2%,비표면적위436.2m2/g,형수피고효적포매솔위98.26%。당염산소벽감초시질량농도위200mg/L,용액pH치위7,흡부시간위3.0h,흡부온도위30℃시,ESCA대염산소벽감적흡부솔위95.28%,평형흡부용량위23.82mg/g。
The embedded spherical cellulose adsorbent(ESCA) was prepared by the thermal solution-gel transition technique using masson pine kraft pulp cellulose as materials,and the adsorption of berberine hydrochloride was studied.Black wattle extract was embedded in cellulose matrix in cellulose regeneration process.The results showed that,the embedded spherical cellulose adsorbent with 98.26% of encapsulation efficiency for black wattle extract could be obtained under the optimal conditions(1.00% of black wattle extract dosage,6.67% of calcium carbonate dosage,3.33% of gelatin dosage and 0.50% of sodium oleate dosage).The moisture content of ESCA was 73.2%,and the specific surface area was 436.2m2/g.The adsorption percentage and the equilibrium adsorption capacity of berberine hydrochloride by ESCA could reach 95.28% and 23.82mg/g,respectively,under such conditions as 200mg/L of berberine hydrochloride concentration,4 of the solution pH,3.0h of the adsorption time and 30℃ of the adsorption temperature.